Failure Analysis of Cemented Carbide Drawing Die AITranslate
Abstract AITranslate
Failure analysis is made of cemented carbide die for drawing copper tube by scanning electron microscopy,etc.It was indicated that grain abrasion and adhesive abrasion were the main types of failure in the drawing die under boundary lubrication and dry friction.Based on the analysis of surface abrasion morphology and action of cyclic load and friction heat of the drawing die,theoretical analysis is made of its failure behavior.Based on the cause of the failures,exploratory suggestion is made for longer service life of the drawing die.
KeyWords AITranslate
1严宏志.[D].中南工业大学,1998.4.
1杨瑱,邵双全,刘永利,申修沇,高建忠,杨义佳.毛细管内表面粗糙度对除湿机性能影响的试验研究[J].流体机械,2011,39(1):65-67. 被引量：5
2唐伟东,张士宏,林涛,刘劲松,程大勇.游动芯头拉拔模具失效分析[J].材料科学与工艺,2012,20(3):109-112. 被引量：3
3马涛,杨学锋,姚孔,李运玺,王呈敏.添加MWCNTs陶瓷拉拔模具材料的摩擦特性研究[J].人工晶体学报,2015,44(9):2583-2589.
4徐华敏,吴礼,曾延琦.盘拉TP2铜管坯的“划伤”缺陷研究[J].铜业工程,2019,0(3):20-22. 被引量：1
1李松玲.YJ19B卷烟机风室导轨的改进[J].包装与食品机械,2012,30(3):70-71. 被引量：2
2杨树恒,王芳,刘劲松.游动芯头多道次拉拔加工率对TP2铜管材力学性能的影响研究[J].沈阳理工大学学报,2013,32(3):30-32. 被引量：1
3冯淳,冯海芃.制冷与空调系统中毛细管流量的测试方法研究[J].流体机械,2013,41(7):78-80. 被引量：4
4谷德军,金梧凤,裴凤,刘艳超.毛细管重力循环供冷末端装置及运行性能研究[J].流体机械,2013,41(9):54-60. 被引量：5
5黄美玲.毛细管粗糙度对空调器性能影响的试验研究[J].制冷与空调,2014,14(4):66-68.
6刘劲松,陈大勇,张士宏.基于数值模拟的TP2铜管三联拉工艺优化[J].中国有色金属学报,2015,25(2):458-465. 被引量：9
7魏睆,缪小平,张翼,魏子杰,羊雷,邵光明.地下工程调温除湿机的节能优化方案及性能模拟研究[J].流体机械,2017,45(3):75-80. 被引量：3
8余志远,王昌,汶斌斌,艾迪,刘汉源,于振涛.AZ31镁合金管材游动芯头拉拔有限元模拟[J].材料导报,2018,32(16):2778-2782. 被引量：1
9唐海龙,蔡锋,黄世新,段金梅,李廷鹏,汪红燕,孙永岗,张宗彬.圆盘拉拔紫铜管杂物压入类缺陷研究[J].铜业工程,2023(4):115-121.
1陈跃勤,唐英.GCr15钢不同热处理后的磨损特征[J].金属热处理,2000,25(11):18-20. 被引量：4
2杨锴.主动圆柱齿轮与从动圆柱齿轮磨损分析[J].热处理技术与装备,2010,31(6):41-43.
3朱金元,濮卫国.周期蠕变下材料强化的研究[J].五钢科技,1992(2):45-50.
4丁津原,赵民.工具钢表面激光熔覆耐磨性试验研究[J].东北大学学报：自然科学版,2002,23(7):687-690.
5徐经忠,丁厚福.衬板用钢在石英砂介质中的冲击腐蚀磨损行为[J].合肥工业大学学报：自然科学版,2005,28(1):49-52. 被引量：1
6王家庆,杜晓东,丁厚福,王凯,孙国栋,满达虎.腐蚀条件下以锰代镍低碳高合金钢的冲击磨损性能及机制[J].钢铁研究学报,2007,19(9):50-53. 被引量：2
7孙建锋,张毅.探究工程机械用钢焊接接头组织与成分[J].中国科技期刊数据库 工业B,2015,0(4):313-313.
8丁厚福,卢书媛,崔方明,陈翌庆.冶金矿山湿式磨机衬板钢冲击腐蚀磨损行为的研究[J].兵器材料科学与工程,2003,26(6):31-35. 被引量：11
9冯爱新,何叶,杨润,薛伟,曹宇鹏,李峰平,田良,谢华锟,陈云.硬质合金基体微织构对TiAlN涂层摩擦性能的影响[J].材料热处理学报,2015,36(9):161-166. 被引量：3
10何奖爱,李书琴,辛启斌,查向东.水韧处理温度对含硼超高锰钢组织和性能的影响[J].金属热处理,2009,34(5):83-85. 被引量：3
Basic Information:
DOI：
Chinese Library Classification Number:TG76[金属学及工艺—刀具与模具]
Citation Information:
Failure analysis is made of cemented carbide die for drawing copper tube by scanning electron microscopy,etc.It was indicated that grain abrasion and adhesive abrasion were the main types of failure in the drawing die under boundary lubrication and dry friction.Based on the analysis of surface abrasion morphology and action of cyclic load and friction heat of the drawing die,theoretical analysis is made of its failure behavior.Based on the cause of the failures,exploratory suggestion is made for longer service life of the drawing die.
quote
| GB/T 7714-2015 | [1] HUA You-lu, ZHANG Shi-hong, ZHANG Jin-li. Failure Analysis of Cemented Carbide Drawing Die[J]. Rare Metals and Cemented Carbides, 2003(3): 12-14. |
| MLA | [1] HUA You-lu, et al., "Failure Analysis of Cemented Carbide Drawing Die." Rare Metals and Cemented Carbides, no. 3, 2003, pp. 12-14. |
| APA | [1] HUA You-lu, ZHANG Shi-hong, & ZHANG Jin-li. (2003). Failure Analysis of Cemented Carbide Drawing Die. Rare Metals and Cemented Carbides(3), 12-14. |
| IEEE | [1] HUA You-lu, ZHANG Shi-hong, and ZHANG Jin-li, "Failure Analysis of Cemented Carbide Drawing Die," Rare Metals and Cemented Carbides, no. 3, pp. 12-14, 2003. keywords: {drawing die;cemented carbide;failure analysis} |