Evolution of In783 alloy in microstructure and properties enduring different service times AITranslate

School of Material Science and Engineering;School of Material Science and Engineering;School of Material Science and Engineering;School of Material Science and Engineering
AITranslate
Publisher: Youke Publish Co., Ltd.
Share Citation Information Add to Favorites

    Scan to share on WeChat or Moments

Use WeChat scan.
Share with WeChat friends or Moments

Abstract AITranslate

Impact, tensile, and fatigue tests were performed in In783 alloy serving 4000, 23,000 and 48,000 h. The microstructure was then analysed by optical microscopy(OM), scanning electron microscopy(SEM), and transmission electron microscopy(TEM) to probe the relationship between microstructure and properties. The results show that a new Ni5Al3 phase is found, which grows gradually in β phase with serving time increasing,destroying the martensitic structure of the β phase, and degenerating the toughness of the β phase(approximately13.88% reduction). Therefore, the degradation of the βphase results in a sharp dropping of the resistance to stress accelerated grain boundary oxygen(SAGBO) during serving;thus, the intergranular fracture morphology degree increases with duration of service(almost 40% increase from the fractured surface). In addition, the strength of alloy will be gradually enhanced when the γ'phase becomes relatively bulky with serving time increasing due to considerable distortion of the dislocations as a result of the spacing of individual particles, in which any movement of the dislocation will have to overcome a larger number of obstacles per unit length.

KeyWords AITranslate

In783 MICROSTRUCTURE PROPERTIES βphase Ni5Al3phase

1J.H.Thndermann(Inco Alloys International, Inc., Huntington, WV 25705, USA ).DEVELOPMENT OF INCONEL~ ALLOY 783,A LOW THERMAL EXPANSION,CRACK GROWTH RESISTANT SUPERALLOY[J].Acta Metallurgica Sinica(English Letters),1996,9(6):503-507. 被引量:25

2WEI Zhigang,ZHAO Yating,XIE Wei,CHEN Guosheng.Effect of intergranular β phase on the rupture plasticity of the low expansion Inconel 783 superalloy[J].Baosteel Technical Research,2011,5(4):16-20. 被引量:2

3Hong-Yu Qi,Ji-Shen Yang,Xiao-Guang Yang,Shao-Lin Li.Low-cycle fatigue behavior of a directionally solidified Ni-based superalloy subjected to gas hot corrosion pre-exposure[J].Rare Metals,2019,38(3):227-232. 被引量:6

4Jiang-Dong Cao,Jun-Song Zhang,Yin-Qun Hua,Zhen Rong,Rui-Fang Chen,Yun-Xia Ye.High temperature oxidation behavior of Ni-based superalloy GH586 in air[J].Rare Metals,2017,36(11):878-885. 被引量:6

5M.I.El-Hofy(Physics Department, Faculty of Science, Menoufia University, Shebin El-Kom, Egypt)A.M.Donia(Chemistry Department, Faculty of Science, Menoufia University, Shebin El-Kom, Egypt)M.M.Abou-Sekkina(Chemistry Department, Faculty of Science, Taota Un.Electrical Investigation of Some Silver Containing Ceramics Obtained from Coprecipitated Oxalates[J].Journal of Materials Science & Technology,1999,15(1):87-90. 被引量:20

6Xiao-Dai Yue,Jia-Rong Li,Xiao-Guang Wang.The microstructure of a single crystal superalloy after different aging heat treatments[J].Rare Metals,2018,37(3):210-216. 被引量:7

1徐雄,李钊,万志鹏,韦康,王涛,张新房.长期时效对低膨胀高温合金GH2909性能的影响[J].材料研究学报,2021,35(5):330-338. 被引量:3

1李钊,江河,王涛,付书红,张勇.GH2909低膨胀高温合金热处理中的组织演变行为[J].金属学报,2022,58(9):1179-1188. 被引量:2

2杨浩,王方军,刘海定,赵莎莎,黄海堂,李三梅,尹雪雪.Al、Si元素含量对高温低膨胀合金组织及性能的影响[J].功能材料,2023,54(12):12199-12205. 被引量:1

3吕涛,刘芳,刘畅,董德秀,张伟红,蔡桂喜.GH907合金机匣锻环的超声衰减性能与其组织的关系[J].材料研究学报,2024,38(1):14-22.

1王庆峰.超超临界机组In783合金螺栓早期断裂原因及其应用建议[J].理化检验(物理分册),2023,59(12):69-73.

2Chris Palmer.光学显微镜分辨率提升至亚纳米级[J].Engineering,2023,31(12):11-14.

3Bing Wang,Hong-Lin Zhang,Bin Xu,Hai-Yang Jiang,Ming-Yue Sun,Dian-Zhong Li.Sensitivity of the Impact Toughness and Microstructure of 15CrNi3MoV Steel Under Different Quenching Rates[J].Acta Metallurgica Sinica(English Letters),2023,36(10):1735-1748.

4Mu Meng,Honglei Zhang,Zhi Gao,Genxing Lei,Jianmin Yu.Effect of aging treatment on the precipitation transformation and age hardening of Mg-Gd-Y-Zn-Zr alloy[J].Journal of Magnesium and Alloys,2023,11(12):4628-4643. 被引量:1

5Shuang-Yin Zhang,Liang Liu,Rui Bao,Jian-Hong Yi,Sheng-Da Guo.Attaining synergetic equilibrium of electrical conductivity and tensile strength in GQDs@GN/Cu composites through multi-scale intragranular and intergranular reinforcements[J].Rare Metals,2024,43(1):366-379.

6Xin Yu,Yuye Tan,Weidong Song,John Kemeny,Shengwen Qi,Bowen Zheng,Songfeng Guo.Damage evolution of rock-encased-backfill structure under stepwise cyclic triaxial loading[J].Journal of Rock Mechanics and Geotechnical Engineering,2024,16(2):597-615. 被引量:1

7Yanlong Ma,Lei Liu,Xinxin Zhang,Fei Guo,Xiaorong Zhou,Mingbo Yang,Jingfeng Wang.Effect of air-formed film on corrosion behavior of magnesium-lithium alloys[J].Journal of Magnesium and Alloys,2023,11(11):4325-4337.

8En-Qiang Linghu.New direction for surgery:Super minimally invasive surgery[J].World Journal of Gastroenterology,2024,30(12):1676-1679.

9Xu Yuanyu,Chen Yuxu,Zhang Jingqing,Zhao Zhimin,Yang Depo,Xu Xinjun,Wang Shidong.Research Progress on Application of Borneol As Permeation Enhancer in Functional Cosmetics[J].China Detergent & Cosmetics,2024,9(1):71-75.

10YANG Peng,ZHANG Shicheng,ZOU Yushi,LI Jianmin,MA Xinfang,TIAN Gang,WANG Junchao.Fracture propagation,proppant transport and parameter optimization of multi-well pad fracturing treatment[J].Petroleum Exploration and Development,2023,50(5):1225-1235.

Basic Information:

DOI:

Chinese Library Classification Number:TG132.3[一般工业技术—材料科学与工程]

Citation Information:

Impact, tensile, and fatigue tests were performed in In783 alloy serving 4000, 23,000 and 48,000 h. The microstructure was then analysed by optical microscopy(OM), scanning electron microscopy(SEM), and transmission electron microscopy(TEM) to probe the relationship between microstructure and properties. The results show that a new Ni5Al3 phase is found, which grows gradually in β phase with serving time increasing,destroying the martensitic structure of the β phase, and degenerating the toughness of the β phase(approximately13.88% reduction). Therefore, the degradation of the βphase results in a sharp dropping of the resistance to stress accelerated grain boundary oxygen(SAGBO) during serving;thus, the intergranular fracture morphology degree increases with duration of service(almost 40% increase from the fractured surface). In addition, the strength of alloy will be gradually enhanced when the γ'phase becomes relatively bulky with serving time increasing due to considerable distortion of the dislocations as a result of the spacing of individual particles, in which any movement of the dislocation will have to overcome a larger number of obstacles per unit length.

quote

GB/T 7714-2015 [1] Zhong-Shuai Han, Jin-Feng Du, Jun Liang, et al. Rare Metals, 2024(1): 334-341.
MLA [1] Zhong-Shuai Han, et al., Rare Metals, no. 1, 2024, pp. 334-341.
APA [1] Zhong-Shuai Han, Jin-Feng Du, Jun Liang, & Zheng Zhang. (2024). Rare Metals(1), 334-341.
IEEE [1] Zhong-Shuai Han, Jin-Feng Du, Jun Liang, and Zheng Zhang, Rare Metals, no. 1, pp. 334-341, 2024.