Effect of Annealing Temperature on Recrystallization Textures of Tantalum Wires AITranslate
Abstract AITranslate
The recrystallization texture of tantalum wires at 1 100 ℃?1 250 ℃?1 360 ℃?1 500 ℃for 40min was investigated by ODF and the recrystallization mechanic was researched via microstructural and hardness tests.It was found that the recrystallization was completed and the fine grain appeared at 1 360 ℃,the texture component consisted of {110} <001> ,which had a 27°-<110>orientation relationship to the deformation textute {112}<110>.At 1 500 ℃,the exaggerated growth occurred,and a new texture{441}<110>with a 27°<110>orientation relationship to the primary texture{110}<001>was found.A recrystallization model of bcc metal was proposed to explain it.
KeyWords AITranslate
1张新明,张少睿,周卓平,舒永春.钽丝的拉拔及退火织构[J].中国有色金属学报,1999,9(4):774-778. 被引量：11
1万庆峰,王德志,赵兵.掺杂与钽丝毛刺的关系研究[J].稀有金属,2008,32(3):381-386. 被引量：1
2黄元春,谢成,唐建国,邓运来.不同轧制方式对铌箔微观组织和织构的影响[J].中南大学学报：自然科学版,2013(2):501-507. 被引量：2
1李继文,杨松涛,魏世忠,张国赏,徐流杰,U.轧制方式和变形量对纯钼板坯微观组织和织构的影响[J].稀有金属,2014,38(3):348-353. 被引量：12
2张洪刚,雒国清.大球磨机在高压钽锭上的应用[J].世界有色金属,2016,0(9):141-141.
3潘文高,陈炜晔,吴澜尔.钽材轧制和再结晶织构演变研究进展[J].材料导报,2016,30(21):150-156.
1郭磊,王志法.加工方法对钽板力学性能以及织构的影响[J].稀有金属与硬质合金,2005,33(3):18-22. 被引量：6
2袁韧,张新明,周卓平.钽丝的织构和再结晶行为研究[J].材料导报,2002,16(6):68-70. 被引量：2
3郭俊清,李庆春.快速凝固条件下的共晶生长理论[J].金属科学与工艺,1990,9(2):71-76.
4张杰,蔡庆伍,武会宾,樊学华,张明洁.E690海洋平台用钢力学性能和海洋大气腐蚀行为[J].北京科技大学学报,2012,34(6):657-665. 被引量：23
5王超群,王宁,沈惠珠,金红政,方瑛.电子铝箔立方面织构的测试方法[J].物理测试,1998,16(6):14-18.
6曹寒松.提高细径钽丝抗脆性的研究[J].稀有金属与硬质合金,1998,26(3):16-21. 被引量：1
7张新明,孟亚,周卓平,周鸿章.Fe杂质对高纯铝箔再结晶织构及比电容的影响[J].中国有色金属学报,1999,9(1):19-24. 被引量：46
8朱一民,赵晓红,严心羽.快速漏流分选仪[J].测控自动化,2005(1):51-52.
9刘建清,李荐,戴艳阳,钟海云.固体钽电解电容器研究发展趋势[J].稀有金属与硬质合金,2002,30(2):41-44. 被引量：6
10范雄,源可珊,李穗湘,何惠珍.三种硅钢片的分析比较[J].广东工业大学学报,1994,11(1):13-23.
Basic Information:
DOI：
Chinese Library Classification Number:TM535.1[电气工程—电器];TG146.416[金属学及工艺—金属材料]
Citation Information:
The recrystallization texture of tantalum wires at 1 100 ℃?1 250 ℃?1 360 ℃?1 500 ℃for 40min was investigated by ODF and the recrystallization mechanic was researched via microstructural and hardness tests.It was found that the recrystallization was completed and the fine grain appeared at 1 360 ℃,the texture component consisted of {110} <001> ,which had a 27°-<110>orientation relationship to the deformation textute {112}<110>.At 1 500 ℃,the exaggerated growth occurred,and a new texture{441}<110>with a 27°<110>orientation relationship to the primary texture{110}<001>was found.A recrystallization model of bcc metal was proposed to explain it.
quote
| GB/T 7714-2015 | [1] YUAN Ren, ZHANG Xin-ming, ZHOU Zhuo-ping. Effect of Annealing Temperature on Recrystallization Textures of Tantalum Wires[J]. Rare Metals and Cemented Carbides, 2002(3): 17-21. |
| MLA | [1] YUAN Ren, et al., "Effect of Annealing Temperature on Recrystallization Textures of Tantalum Wires." Rare Metals and Cemented Carbides, no. 3, 2002, pp. 17-21. |
| APA | [1] YUAN Ren, ZHANG Xin-ming, & ZHOU Zhuo-ping. (2002). Effect of Annealing Temperature on Recrystallization Textures of Tantalum Wires. Rare Metals and Cemented Carbides(3), 17-21. |
| IEEE | [1] YUAN Ren, ZHANG Xin-ming, and ZHOU Zhuo-ping, "Effect of Annealing Temperature on Recrystallization Textures of Tantalum Wires," Rare Metals and Cemented Carbides, no. 3, pp. 17-21, 2002. keywords: {tantalum wires;recrystallization;annealing temperature;texture} |