Investigation on Mechanical Properties and Failure Mechanism of Ti-22Al-15Nb Alloy AITranslate

Beijing Institute of Technology Materials College;Beijing Institute of Technology Materials College;Beijing Institute of Technology Materials College;Beijing Institute of Technology Materials College;Beijing Institute of Technology Materials College
AITranslate
Publisher: Editorial Office of Rare Metals and Cemented Carbides
Share Citation Information Add to Favorites

    Scan to share on WeChat or Moments

Use WeChat scan.
Share with WeChat friends or Moments

Abstract AITranslate

The microstructure and mechanical properties of Ti-Al based alloy with nominal composition of Ti-22Al-15Nb were investigated,and the deformation behavior under quasi-static and dynamic loading con- ditions was also discussed. The results show that as-cast Ti-22Al-15Nb alloy has equiaxed microstructure mainly composed of α2-Ti3 Al phase and B2-Ti2 AlNb phase, and lamellar α2 phase with random orientation is distributed uniformly in B2 matrix. Investigation on mechanical properties shows that the alloy exhibits higher yield strength of 1 100 MPa and higher compressive strength of 1 750 MPa,and better ductility dur- ing dynamic compression rather than quasi-static compression. Failure mechanism analysis shows that shear failure occurs in the alloy during quasi-static compression,and micro-cracks initiate in α2 phase or the boundary between az phase and B2 matrix and extend along the direction of the maximum shear stress to form main cracks, finally leading to alloy failure. Failure mode of the alloy during dynamic compression is adiabatic shear failure,adiabatic shear bands form at an angle of about 45° with the loading direction,and cracks initiate in the shear band and propagate with the increased strain, finally leading to alloy failure.

KeyWords AITranslate

Ti-Al based alloy Ti-22Al-15Nb dynamic mechanical behavior shear band failure mechanism

1宋辉,王忠金,赫晓东.高密度脉冲电流处理对Ti_2AlNb基合金板材的增塑作用(英文)[J].中国有色金属学报:英文版,2013,23(1):32-37. 被引量:6

2Bingqing Chen,Huaping Xiong,Bingbing Sun,Siyi Tang,Shaoqing Guo,Xuejun Zhang.Microstructure Evolution and Tensile Properties of Ti_3Al/Ni-based Superalloy Welded Joint[J].材料科学技术:英文版,2014(7):715-721. 被引量:7

3王克鲁,鲁世强,康永林,董显娟,李鑫.Ti_3Al基合金的热变形行为及加工图[J].稀有金属材料与工程,2011,40(9):1534-1539. 被引量:10

4司玉锋,陈子勇,孟丽华,王肇文,陈玉勇.Ti_3Al基金属间化合物的研究进展[J].特种铸造及有色合金,2003(4):33-35. 被引量:18

5梁晓波,程云君,张建伟,李世琼.热处理对β锻造Ti-22Al—25Nb合金组织和性能的影响[J].中国有色金属学报,2010,20(B10):336-341. 被引量:76

6武英,杨德庄.Ti_3Al基金属间化合物变形行为研究进展[J].宇航材料工艺,1997,27(3):5-12. 被引量:3

7王孟光,孙建科,陈志强.Ti_3Al基合金室温塑性的改善方法[J].稀有金属快报,2007,26(11):7-12. 被引量:7

8曹京霞,许剑伟.(α_2+O+B2)三相Ti_3Al基合金的微观组织与力学性能[J].钛工业进展,2008,25(5):15-19. 被引量:6

9张鹰,李学明,高扬.热处理工艺对Ti_3Al基合金拉伸性能的影响[J].材料工程,1992(4):23-25. 被引量:2

1孙达.Ti-Al系中TiAl和Ti_3Al相层生长动力学和互扩散[J].上海金属:有色分册,1991,12(5):1-6.

2王杰,刘贺,刘丽,张兴铎.308L不锈钢堆焊试板点腐蚀原因分析[J].大型铸锻件,2011(6):23-27. 被引量:4

3高峻,姚泽坤,刘莹莹.电子束焊接热输入对Ti-24Al-15Nb-1.5Mo/TC11双合金焊接接头组织和显微硬度的影响[J].焊接学报,2009,30(7):33-36. 被引量:4

4高华,赵亮,李宏军.轧制工艺对热轧带钢轧辊使用周期的影响[J].河北冶金,2005(4):41-43. 被引量:3

5王邵鹏,王冰,唐立丹,周小平,梁策.电脉冲孕育处理对Al-15Mg_2Si-1Cu合金组织和性能的影响[J].轻合金加工技术,2015,43(7):15-17. 被引量:1

6杨海东.热轧辊破坏机理研究[J].中国金属通报,2015,0(4):41-43. 被引量:2

7韦建军.钢坯牵引剪切机液压泵破坏机理研究[J].液压与气动,1999(3):16-17. 被引量:1

8尹建明,卢斌,李玉兰,杨锐.Ti_2AlNb合金板材的电子束焊接[J].中国有色金属学报,2010,20(B10):325-330. 被引量:17

9刘志,周洪.热障涂层研究进展[J].河海大学常州分校学报,2006,20(3):9-13. 被引量:2

10谭立军,姚泽坤,周伟,郭鸿镇,张建伟.焊后热处理对异种合金摩擦焊件组织与性能的影响[J].金属热处理,2010,35(4):29-32. 被引量:3

Basic Information:

DOI:

Chinese Library Classification Number:TG146.1[金属学及工艺—金属材料]

Citation Information:

The microstructure and mechanical properties of Ti-Al based alloy with nominal composition of Ti-22Al-15Nb were investigated,and the deformation behavior under quasi-static and dynamic loading con- ditions was also discussed. The results show that as-cast Ti-22Al-15Nb alloy has equiaxed microstructure mainly composed of α2-Ti3 Al phase and B2-Ti2 AlNb phase, and lamellar α2 phase with random orientation is distributed uniformly in B2 matrix. Investigation on mechanical properties shows that the alloy exhibits higher yield strength of 1 100 MPa and higher compressive strength of 1 750 MPa,and better ductility dur- ing dynamic compression rather than quasi-static compression. Failure mechanism analysis shows that shear failure occurs in the alloy during quasi-static compression,and micro-cracks initiate in α2 phase or the boundary between az phase and B2 matrix and extend along the direction of the maximum shear stress to form main cracks, finally leading to alloy failure. Failure mode of the alloy during dynamic compression is adiabatic shear failure,adiabatic shear bands form at an angle of about 45° with the loading direction,and cracks initiate in the shear band and propagate with the increased strain, finally leading to alloy failure.

quote

GB/T 7714-2015 [1] SANG Qing-qing, LIU Jin-xu, HAO Yan-jun, et al. Investigation on Mechanical Properties and Failure Mechanism of Ti-22Al-15Nb Alloy[J]. Rare Metals and Cemented Carbides, 2017(2): 45-50.
MLA [1] SANG Qing-qing, et al., "Investigation on Mechanical Properties and Failure Mechanism of Ti-22Al-15Nb Alloy." Rare Metals and Cemented Carbides, no. 2, 2017, pp. 45-50.
APA [1] SANG Qing-qing, LIU Jin-xu, HAO Yan-jun, LI Jian-chong, & LI Shu-kui. (2017). Investigation on Mechanical Properties and Failure Mechanism of Ti-22Al-15Nb Alloy. Rare Metals and Cemented Carbides(2), 45-50.
IEEE [1] SANG Qing-qing, LIU Jin-xu, HAO Yan-jun, LI Jian-chong, and LI Shu-kui, "Investigation on Mechanical Properties and Failure Mechanism of Ti-22Al-15Nb Alloy," Rare Metals and Cemented Carbides, no. 2, pp. 45-50, 2017. keywords: {Ti-Al based alloy;Ti-22Al-15Nb;dynamic mechanical behavior;shear band;failure mechanism}