The nitriding treatment process of Sm-Fe melt-spinning alloy was researched through XRD,SEM and other means.The results show that Sm-Fe melt-spinning ribbons after nitriding are mainly composed of Sm2 Fe17 Nx,α-Fe,Fe2 O3 and Sm2 O3.After nitriding,Sm-Fe melt-spinning ribbons containing noncrystal partially crystallize,but the crystallinity is relatively low or the grains are small,not excessively grown and almost maintaining the grain size of melt-spinning ribbons.There are clearly visible fine grains scattering in the roll surface after nitriding,and the maximum grain size is about 5μm.The white stuff containing nitrides is distributed in disorder at the boundary of spherical particles on the free surface,and the greater the melt-spinning speed,the more the white stuff precipitated in the Sm-Fe ribbons.
KeyWords AITranslate
1罗阳.SmFe_7金属间化合物——新一代磁体的希望[J].粉末冶金工业,2000,10(5):26-31. 被引量：7
2启明.高性能稀土磁体的开发[J].金属功能材料,2007,14(1):41-42. 被引量：9
3李大勇,段焕强.钐铁氮稀土永磁材料产业化进展[J].中国新技术新产品,2012(20):146-148. 被引量：17
4王书桓,袁亮亮,赵定国,高爱民,宋春燕,李彬.Sm_2Fe_(17)型合金氮化工艺的研究进展[J].中国稀土学报,2017,35(3):315-321. 被引量：9
5汪卫华.非晶中“缺陷”——流变单元研究[J].中国科学：物理学、力学、天文学,2014,44(4):396-405. 被引量：10
1徐山雪,潘晶,刘新才,赵丽.淬速对Nd9Fe70Ti3C1Nb3B14快淬薄带晶化相变和磁性能的影响[J].稀有金属,2018,42(5):491-497.
2袁亮亮,高爱民,马海涛,王书桓,赵定国.液态钐铁合金中氮气泡的运动行为[J].热加工工艺,2018,47(13):87-90.
3吃虾要去头 这些海鲜小知识你都知道吗[J].中国食品,2018,0(14):165-165.
4赵永涛,汤安,张红松,张冰,徐晓东.(Sm_(1-x)Al_x)_2Ce_2O_7化合物的热物理性能[J].人工晶体学报,2018,47(7):1480-1485.
5双喷嘴快淬法制得的非晶/晶体Fe55Ni20Cu5P10Si5B5[J].金属功能材料,2018,25(4):44-44.
6吴春姬,王文全,张金宝,侯志鹏.Hf-Co-B-W合金薄带的结构和磁性[J].吉林大学学报：理学版,2018,56(4):991-994.
7王元栋,海侠女,杨扬,车永平.金属材料的表面氮化处理工艺应用与研究[J].世界有色金属,2017,42(16):268-268. 被引量：3
8韩丹.快淬速度对SmCo_(6.9)Hf_(0.1)(CNTs)_(0.05)薄带磁性能的影响[J].天津冶金,2017(5):50-52.
9乔荫颇,李明阳,王答成,沈鹏,周沁,李新宇,陈璞,姬甜.B/Sm共掺杂羟基磷灰石的制备及发光性能[J].陕西科技大学学报,2018,36(4):115-119. 被引量：1
10梅俊,祁焱,徐立红,臧岩,赵栋梁.改进型快淬冷却辊流场及温度场模拟[J].金属功能材料,2018,25(3):1-5. 被引量：1
Basic Information:
DOI：
Chinese Library Classification Number:TG146.45[金属学及工艺—金属材料]
Citation Information:
The nitriding treatment process of Sm-Fe melt-spinning alloy was researched through XRD,SEM and other means.The results show that Sm-Fe melt-spinning ribbons after nitriding are mainly composed of Sm2 Fe17 Nx,α-Fe,Fe2 O3 and Sm2 O3.After nitriding,Sm-Fe melt-spinning ribbons containing noncrystal partially crystallize,but the crystallinity is relatively low or the grains are small,not excessively grown and almost maintaining the grain size of melt-spinning ribbons.There are clearly visible fine grains scattering in the roll surface after nitriding,and the maximum grain size is about 5μm.The white stuff containing nitrides is distributed in disorder at the boundary of spherical particles on the free surface,and the greater the melt-spinning speed,the more the white stuff precipitated in the Sm-Fe ribbons.
quote
| GB/T 7714-2015 | [1] YUAN Liang-liang, GAO Ai-min, ZHANG Kai-xuan, et al. Nitriding Treatment of Sm-Fe Melt-Spinning Alloy[J]. Rare Metals and Cemented Carbides, 2018(4): 59-63. |
| MLA | [1] YUAN Liang-liang, et al., "Nitriding Treatment of Sm-Fe Melt-Spinning Alloy." Rare Metals and Cemented Carbides, no. 4, 2018, pp. 59-63. |
| APA | [1] YUAN Liang-liang, GAO Ai-min, ZHANG Kai-xuan, & WANG Shu-huan. (2018). Nitriding Treatment of Sm-Fe Melt-Spinning Alloy. Rare Metals and Cemented Carbides(4), 59-63. |
| IEEE | [1] YUAN Liang-liang, GAO Ai-min, ZHANG Kai-xuan, and WANG Shu-huan, "Nitriding Treatment of Sm-Fe Melt-Spinning Alloy," Rare Metals and Cemented Carbides, no. 4, pp. 59-63, 2018. keywords: {Sm-Fe alloy;melt-spinning ribbon;nitriding;microstructure;phase analysis} |