Research on Wet Preparation of Nanocrystalline Tungsten Oxide Powder by Roll Ball Milling AITranslate
Abstract AITranslate
Nanocrystalline WO3 powder is prepared by mechanical ball milling. Study is made on the influences of ratio of ball to powder, ratio of solid to liquid,and grinding time on powder characteristics were studied, The influences of ratio of ball to powder and grinding time was very serious. Longer grinding time and bigger ratio of ball to powder would not result in finer powder,but increase of the WC impurity content. Too higher or too lower ratio of solid to liquid is not good for further fineness of WO3. In order to gain higher purity nano WO3 powder ,the best condition of WO3 preparation would be as follows：ratio of ball to powder 1：1,ratio of solid to liquid 1：0. 5,grinding duration 48 h.
KeyWords AITranslate
1Bose A,et al.Development of a new W-Ni-Mn heavy alloy[J].Advances in Powder Metallurgy,1991,6:425.
2李强,李启寿,雷代富,王锡胜.纳米晶W粉和W-Ni-Fe预合金粉的制备[J].稀有金属材料与工程,2004,33(1):70-74. 被引量：4
3Agnihotry S A,et al.Pre-existence of HxWO3 in e-beam deposited WO3 films[J].Solar Energy Materials and Solar Cells,1995,36:289.
4Cantalini C,et al.NO2 sensitivity of WO2 thin film obtained by high vacuum thermal evaporation[J].Sensors and Actuators,1996,B31:81.
5张晖,丁秉钧.纳米复合W-氧化物电极材料的电子发射特性[J].稀有金属材料与工程,2000,29(1):53-56. 被引量：14
1杜伟,周震涛,刘金成.机械活化对碳热还原法LiFePO_4结构与性能的影响[J].电源技术,2011,35(4):385-389.
2朱慧敏,高文元,闫爽,刘贵山,郝洪顺.静电纺丝技术制备无机功能复合纳米纤维的研究进展[J].中国陶瓷工业,2017,24(4):53-56. 被引量：1
1马玥珑,李佳,王虹.静电纺丝制备载药纳米纤维的研究进展[J].哈尔滨理工大学学报,2021,26(5):130-140. 被引量：4
1谭金琨,尹海生.水分,膨润土用量和焦粉粒度影响生球强度的研究[J].唐钢科技,1990(2):18-22.
2谭金琨,尹海生.水分、膨润土用量和焦粉粒度影响生球强度的研究[J].河北冶金,1990(5):5-9. 被引量：1
3高家诚,陈小华,唐祁峰.氟化钙催化碳热还原氧化镁的实验研究[J].功能材料,2012,43(10):1312-1315. 被引量：2
4赵放,张丽英,林涛,吴成义.纳米级WO3粉末制备工艺的研究[J].粉末冶金技术,2004,22(5):289-292. 被引量：7
5吴国友,沈毅,张青龙,朱华.纳米WO_3薄膜材料的制备及掺杂改性研究[J].中国钨业,2005,20(5):29-33. 被引量：1
6吴兴惠,陈占先,李艳峰,周帧来.粉末WO_3烧结体气敏特性的研究[J].传感技术学报,1992(3):44-48. 被引量：7
7卢广锋,郭志猛,张丽英,罗骥,吴成义.溶胶凝胶纳米WO_3的还原特征[J].粉末冶金技术,2006,24(2):122-126. 被引量：2
8韩海涛,尚福亮,杨海涛,高玲.纳米WO_3薄膜的制备方法及其研究现状[J].稀有金属与硬质合金,2006,34(2):48-51. 被引量：9
9胡建华,施雨湘,吴芳.球磨参数对纯金属粉末颗粒尺寸的影响[J].武汉理工大学学报：交通科学与工程版,2002,26(3):343-346. 被引量：4
10徐金龙,张丽英,林涛,吴成义.纳米级WO_3-CuO复合氧化物粉末的制备[J].北京科技大学学报,2004,26(3):293-296. 被引量：2
Basic Information:
DOI：
Chinese Library Classification Number:TF123.111[冶金工程—粉末冶金]
Citation Information:
Nanocrystalline WO3 powder is prepared by mechanical ball milling. Study is made on the influences of ratio of ball to powder, ratio of solid to liquid,and grinding time on powder characteristics were studied, The influences of ratio of ball to powder and grinding time was very serious. Longer grinding time and bigger ratio of ball to powder would not result in finer powder,but increase of the WC impurity content. Too higher or too lower ratio of solid to liquid is not good for further fineness of WO3. In order to gain higher purity nano WO3 powder ,the best condition of WO3 preparation would be as follows：ratio of ball to powder 1：1,ratio of solid to liquid 1：0. 5,grinding duration 48 h.
quote
| GB/T 7714-2015 | [1] HAN Hai-tao, YANG Hai-tao, SHANG Fu-liang, et al. Research on Wet Preparation of Nanocrystalline Tungsten Oxide Powder by Roll Ball Milling[J]. Rare Metals and Cemented Carbides, 2006(4): 22-24. |
| MLA | [1] HAN Hai-tao, et al., "Research on Wet Preparation of Nanocrystalline Tungsten Oxide Powder by Roll Ball Milling." Rare Metals and Cemented Carbides, no. 4, 2006, pp. 22-24. |
| APA | [1] HAN Hai-tao, YANG Hai-tao, SHANG Fu-liang, & GAO Ling. (2006). Research on Wet Preparation of Nanocrystalline Tungsten Oxide Powder by Roll Ball Milling. Rare Metals and Cemented Carbides(4), 22-24. |
| IEEE | [1] HAN Hai-tao, YANG Hai-tao, SHANG Fu-liang, and GAO Ling, "Research on Wet Preparation of Nanocrystalline Tungsten Oxide Powder by Roll Ball Milling," Rare Metals and Cemented Carbides, no. 4, pp. 22-24, 2006. keywords: {mechanical ball milling;nanocrystalline W03 powder;granularity analysis} |