Analysis of Causes of Corrosion Cracking on the Heating Pipe of APT Crystallizer AITranslate
Abstract AITranslate
The heating pipe of stainless-steel APT crystallizer cracks and leaks when heat conducting oil is used as its heating medium.Therefore,the causes of crack formation are analyzed by macroscopic examination,component analysis and parameter test.And it is pointed out that stress and Cl-from heat conducting oil are the main causes.Some specific measures to resolve the problem are suggested.
KeyWords AITranslate
1吴剑.不锈钢的腐蚀破坏与防蚀技术——(一)点腐蚀的形成条件、形貌特征及其预防[J].腐蚀与防护,1997,18(1):38-42. 被引量：40
2张平柱,刘兴华,胡石林,张伟国.316Ti不锈钢环境敏感断裂起裂时间研究[J].原子能科学技术,1999,33(2):141-146. 被引量：3
1张勇,袁中学.导热油代替间接蒸汽加热的研究与应用[J].中国科技博览,2013(8):35-35.
2李人杰,李培杰,罗业朗.一种新型镁合金压铸模具温控机的设计开发[J].特种铸造及有色合金,2005,25(6):370-371. 被引量：1
3赵欣,马天军,徐文亮,孙敏.Incoloy 800镍基合金加热管腐蚀性能研究[J].上海金属,2016,38(3):11-14. 被引量：3
4冯关明,赵巧良.氩电联焊在改造导热油管路中的应用[J].焊接技术,2014,43(4):73-75.
5张洪武.避免导热油变质失效的措施[J].特种设备安全技术,2008(1):32-33.
6石幼华.紧张热定形机辊筒加热形式分析及探讨[J].纺织机械,2009(4):15-17.
7王会廷,史加文,潘洪波,沈晓辉,曹杰.液体介质传热渐进温成形研究[J].锻压技术,2016,41(2):21-24. 被引量：6
8朱洪军,吉英哲,包毅斐.PQ35发动机支架压铸模具的设计和改进[J].特种铸造及有色合金,2007,27(5):367-369. 被引量：1
9曹军.苯酐装置切换冷凝器改造的几点建议[J].化工中间体,2009,5(9):49-50. 被引量：1
10明卫平,张怡悦,王传志,许元,刘欣芳,熊金平.不锈钢截止阀波纹管组件腐蚀开裂失效分析[J].表面技术,2016,45(2):28-33. 被引量：10
Basic Information:
DOI：
Chinese Library Classification Number:TG174.22[金属学及工艺—金属表面处理]
Citation Information:
The heating pipe of stainless-steel APT crystallizer cracks and leaks when heat conducting oil is used as its heating medium.Therefore,the causes of crack formation are analyzed by macroscopic examination,component analysis and parameter test.And it is pointed out that stress and Cl-from heat conducting oil are the main causes.Some specific measures to resolve the problem are suggested.
quote
| GB/T 7714-2015 | [1] LI Jian-hui. Analysis of Causes of Corrosion Cracking on the Heating Pipe of APT Crystallizer[J]. Rare Metals and Cemented Carbides, 2011(2): 57-59. |
| MLA | [1] LI Jian-hui. "Analysis of Causes of Corrosion Cracking on the Heating Pipe of APT Crystallizer." Rare Metals and Cemented Carbides, no. 2, 2011, pp. 57-59. |
| APA | [1] LI Jian-hui. (2011). Analysis of Causes of Corrosion Cracking on the Heating Pipe of APT Crystallizer. Rare Metals and Cemented Carbides(2), 57-59. |
| IEEE | [1] LI Jian-hui, "Analysis of Causes of Corrosion Cracking on the Heating Pipe of APT Crystallizer," Rare Metals and Cemented Carbides, no. 2, pp. 57-59, 2011. keywords: {APT crystallizer;heat exchanger;316Ti heating pipe;heat conducting oil;crack;stress corrosion;Cl} |