Study on Process of Scheelite Synthesis from Wolframite and Calcium Carbonate AITranslate
Abstract AITranslate
The process was studied of scheelite synthesis by calcination of wolframite and calcium carbon- ate,and the effects were systematically investigated of calcium carbonate dosage, calcining temperature and calcining time on seheelite synthesis from wolframite. When calcium carbonate dosage is 1.6 times the the- oretical amount,calcining temperature is 800 ℃ and calcining time is 2 h, wolframite can be completely synthesized into scheelite.
KeyWords AITranslate
1万林生,邓登飞,赵立夫,李红超,徐国钻,梁勇.钨绿色冶炼工艺研究方向和技术进展[J].有色金属科学与工程,2013,4(5):15-18. 被引量：18
2万林生,赵立夫,李红超.崇义章源钨业APT绿色冶炼的技术进步和发展[J].中国钨业,2012,27(1):47-49. 被引量：13
3万林生,徐国钻,严永海,聂华平,赵立夫,肖学有.中国钨冶炼工艺发展历程及技术进步[J].中国钨业,2009,24(5):63-66. 被引量：20
4万林生,赵立夫,黄泽辉,等.一种铵盐分解白钨矿的方法[P].中国专利:102154547B,2013-01-16.
5赵立夫,李红超,徐国钻,等.将黑钨矿转型为白钨矿的方法[P].中国专利:102649995A,2012-08-29.
6万林生,舒柳飞,赵立夫,谌勇明,李红超.黑钨矿与碳酸钙人工合成白钨的反应过程和机理[J].稀有金属与硬质合金,2014,42(2):1-4. 被引量：3
1万林生,舒柳飞,赵立夫,谌勇明,李红超.黑钨矿与碳酸钙人工合成白钨的反应过程和机理[J].稀有金属与硬质合金,2014,42(2):1-4. 被引量：3
2刘永生,徐义.等摩尔法制备粗颗粒人工合成白钨[J].中国钨业,1992(12):18-22.
3徐本军,符秀锋,陈坤.用粉煤灰制取白炭黑的工艺现状[J].湿法冶金,2013,32(3):135-137. 被引量：4
4杨卜,彭金辉,汪云华,张世敏,范兴祥,郭胜惠.微波辐射煅烧法制取氧化锌新工艺[J].新技术新工艺,2005(12):47-48. 被引量：1
5李报厚,张登君,张冠东.共沉淀—─煅烧法制备CeO_2-Y_2O_3-ZrO_2陶瓷粉末[J].化工冶金,1997,18(1):27-31. 被引量：7
6郑林义,徐初阳,张明旭,王超瑞.煤矸石低温煅烧法制备白炭黑[J].矿冶工程,2010,30(5):100-103. 被引量：8
7李裕芳,赖道玉.不同颗粒人造白钨的制取[J].中国钨业,1990(11):11-14. 被引量：2
8杜光超,尹丹凤,孙朝晖,景涵,陈海军,唐红建,余彬,王唐林.固相煅烧法制备钒酸铋颜料工艺研究[J].钢铁钒钛,2016,37(5):35-42. 被引量：4
9杨传仁,秦广宇,周大雨,游文南,苟富均.B位离子共沉-煅烧法制备Ba(Mg_(1/3)Ta_(2/3))O_3微波陶瓷材料[J].硅酸盐学报,1999,27(4):437-444. 被引量：4
10晏心,湛菁.尖晶石NiCo_2O_4粉末的制备研究及其应用现状[J].金属材料与冶金工程,2013,41(4):57-62.
Basic Information:
DOI：
Chinese Library Classification Number:TF841.1[冶金工程—有色金属冶金]
Citation Information:
The process was studied of scheelite synthesis by calcination of wolframite and calcium carbon- ate,and the effects were systematically investigated of calcium carbonate dosage, calcining temperature and calcining time on seheelite synthesis from wolframite. When calcium carbonate dosage is 1.6 times the the- oretical amount,calcining temperature is 800 ℃ and calcining time is 2 h, wolframite can be completely synthesized into scheelite.
quote
| GB/T 7714-2015 | [1] WAN Lin-sheng, PAN Ming-ran, CHEN Yong-ming, et al. Study on Process of Scheelite Synthesis from Wolframite and Calcium Carbonate[J]. Rare Metals and Cemented Carbides, 2014(6): 1-3. |
| MLA | [1] WAN Lin-sheng, et al., "Study on Process of Scheelite Synthesis from Wolframite and Calcium Carbonate." Rare Metals and Cemented Carbides, no. 6, 2014, pp. 1-3. |
| APA | [1] WAN Lin-sheng, PAN Ming-ran, CHEN Yong-ming, ZHAO Li-fu, & LI Hong-chao. (2014). Study on Process of Scheelite Synthesis from Wolframite and Calcium Carbonate. Rare Metals and Cemented Carbides(6), 1-3. |
| IEEE | [1] WAN Lin-sheng, PAN Ming-ran, CHEN Yong-ming, ZHAO Li-fu, and LI Hong-chao, "Study on Process of Scheelite Synthesis from Wolframite and Calcium Carbonate," Rare Metals and Cemented Carbides, no. 6, pp. 1-3, 2014. keywords: {wolframite;calcium carbonate;calcination;synthesis scheelite} |