Effects of a New Type of Grain Growth Inhibitor on Sintering Behavior of Nanometer Cemented Carbide AITranslate
Abstract AITranslate
Study is made of the effects and effecting mechanisms of a new type of grain growth inhibitor on vacuum sintering behavior of nanometer cemented carbide.The results show that the new grain-growth inhibitor can improve sintering densification process.The addition of the new grain-growth inhibitor into traditional transitional element carbides,resulteding composite inhibitors,which are much more effective and can induce oriented WC grain growth obviously during sintering.For WC-10Co-0.8VC/Cr_3C_2 powders with 0.1% mass content of the new additive,the density of 14.48 g/cm^3 can be achieved after sintering at 1 375 ℃ for 30 min, corresponding to the grain size of 160 nm and the micro-hardness of 2 150 MPa.
KeyWords AITranslate
1Tracey V A. Nickel in hardmetals[J].International Journal of Refractory Metals & Hard Materials,1992, 11(1): 1.
2王辉平,胡茂中.纳米技术与硬质合金[J].中国钨业,2001,16(2):30-32. 被引量：35
3Kear B H,et al.Chemical processing and applications for nanostructured materials[J].Nanostructured Materials, 1995,14(6):227.
4马学鸣,赵凌,嵇罡,董远达.机械合金化制备WC-Co纳米硬质合金[J].上海大学学报：自然科学版,1998,4(2):156-160. 被引量：20
5Azcona A,et al.Hot isostatic pressing of ultrafine tungsten carbide-cobalt hardmerals[J].Journal of Materials Science, 2002,37:4 189.
6Sun J,et al.Characterizations of ball-Milled nanocrystalline WC-Co composite powders and subsequently rapid hot pressing sintered cermets[J].Materials Letters,2003,57:3 140.
7Wang S W,et al.Densification of Al2O3 powder using spark plasma sintering[J].Journal of Material Research,2000,15(4):982.
8周健,程吉平,袁润章,章韵瑾,邱进宇.微波烧结WC Co细晶硬质合金的工艺与性能[J].中国有色金属学报,1999,9(3):465-468. 被引量：57
9Sadangi R K,et al.Grains growth inhibition in liquid phase sintered nanophase WC/Co alloys[J].Powder Metallurgy International,1999,(1):27.
10王社权.影响超细硬质合金性能的几个因素[J].硬质合金,2000,17(1):9-12. 被引量：46
1姜爱民,蒋显全,陈巧旺,陈异.晶粒长大抑制剂在硬质合金中的应用概况[J].硬质合金,2010,27(4):252-257. 被引量：13
2鲍立强,张少华.WC—Co硬质合金低压烧结工艺的探索[J].中国科技博览,2013(31):609-609.
3谷曼,王德广,焦明华,俞建卫,吴玉程.铁基粉末温压过程中的致密化[J].材料热处理学报,2014,35(6):15-19. 被引量：6
1徐涛.硬质合金高端产品及新材料发展趋势分析[J].硬质合金,2011,28(6):395-402. 被引量：40
2李亚军,栾道成,王正云,左洪松,秦琴,赵太源.烧结工艺对超细WC-6%Co-0.6%(VC/Cr_3C_2/TaC)硬质合金性能的影响[J].硬质合金,2012,29(1):24-28. 被引量：5
3李延俊,廖立,谢克难,孟祉含.超细WC/Co粉末及其烧结体的制备与表征[J].四川化工,2013,16(1):5-8.
4秦琴.稀土Y_2O_3对WC-6%Co超细硬质合金组织及性能的影响[J].硬质合金,2013,30(1):14-18. 被引量：12
5肖广涛,刘颖,叶金文,谢鸿.(W,Ta)C复合碳化物含量对WC-10Co硬质合金显微结构和力学性能的影响[J].粉末冶金技术,2013,31(5):355-359. 被引量：3
6钟志强,郑海华,欧阳水林,陈瀚.论七面体球磨介质的球磨效率及对合金组织性能的影响[J].有色金属科学与工程,2014,5(3):60-64. 被引量：1
7陈慧.Y_2O_3对YG10超细硬质合金组织和性能的影响[J].粉末冶金技术,2015,33(1):8-12. 被引量：3
8陈小怡,黄华伟,洪震.Y_2O_3对硬质合金晶粒尺寸和摩擦磨损性能的影响[J].粉末冶金技术,2015,33(1):35-38. 被引量：4
9张豪,叶金文,刘颖,马世卿.开放体系下碳热还原氮化法制备(Cr,Ta)_2CN固溶体粉末的研究[J].功能材料,2015,46(B06):71-74.
10罗致,李小波,谢浪,陈琛.Mo_2NiB_2基金属陶瓷的研究进展[J].材料导报,2016,30(7):86-90. 被引量：3
1苏铁健,王富耻,李树奎,王鲁.钢的热导率与化学成分和温度的关系[J].兵器材料科学与工程,2004,27(5):14-16. 被引量：16
2轩勤生.硼硅复合抑制剂对焦炭热态性能的实验研究[J].中州煤炭,2014(10):114-116.
3李炯义,曹顺华,林信平.硬质合金中的晶粒长大抑制剂[J].硬质合金,2004,21(1):56-60. 被引量：23
4刘书祯.超细晶硬质合金晶粒长大抑制剂的研究[J].稀有金属与硬质合金,2007,35(4):51-56. 被引量：21
5朱文辉,罗堪昌,李隆,李祖鑫,朱敏.Mg/MmNi_(5-x)(CoAlMn)_x复合储氢合金的机械合金化制备[J].功能材料,1999,30(3):271-273. 被引量：5
6Choi.,K,唐丹.添加VC对WC—Co合金显微结构形成的影响：抑制晶粒长大的机理[J].国外难熔金属与硬质材料,2001,17(1):21-25. 被引量：1
7全峰,周建,刘伟波,刘桂珍.VC/Cr_3C_2对微波烧结超细WC-10Co性能的影响[J].武汉理工大学学报,2007,29(12):49-51. 被引量：5
8雷贻文,孙荣禄,吴恩熙,唐英.VC/Cr_3C_2添加剂对超细硬质合金组织及性能的影响(英文)[J].稀有金属材料与工程,2009,38(A01):229-233. 被引量：8
9雷贻文,吴恩熙.VC/Cr_3C_2添加剂与烧结温度对超细WC-12Co硬质合金的影响[J].材料科学与工艺,2010,18(3):405-409. 被引量：7
10LEI Yiwen,WU Enxi.Sintering characteristics and microstructure of WC-Co-VC/Cr_3C_2 ultrafine cemented carbides[J].稀有金属：英文版,2009,28(5):482-486. 被引量：3
Basic Information:
DOI：
Chinese Library Classification Number:TF125.3[冶金工程—粉末冶金]
Citation Information:
Study is made of the effects and effecting mechanisms of a new type of grain growth inhibitor on vacuum sintering behavior of nanometer cemented carbide.The results show that the new grain-growth inhibitor can improve sintering densification process.The addition of the new grain-growth inhibitor into traditional transitional element carbides,resulteding composite inhibitors,which are much more effective and can induce oriented WC grain growth obviously during sintering.For WC-10Co-0.8VC/Cr_3C_2 powders with 0.1% mass content of the new additive,the density of 14.48 g/cm^3 can be achieved after sintering at 1 375 ℃ for 30 min, corresponding to the grain size of 160 nm and the micro-hardness of 2 150 MPa.
quote
| GB/T 7714-2015 | [1] LIN Xin-ping, CAO Shun-hua, LI Jiong-yi. Effects of a New Type of Grain Growth Inhibitor on Sintering Behavior of Nanometer Cemented Carbide[J]. Rare Metals and Cemented Carbides, 2004(4): 4-9. |
| MLA | [1] LIN Xin-ping, et al., "Effects of a New Type of Grain Growth Inhibitor on Sintering Behavior of Nanometer Cemented Carbide." Rare Metals and Cemented Carbides, no. 4, 2004, pp. 4-9. |
| APA | [1] LIN Xin-ping, CAO Shun-hua, & LI Jiong-yi. (2004). Effects of a New Type of Grain Growth Inhibitor on Sintering Behavior of Nanometer Cemented Carbide. Rare Metals and Cemented Carbides(4), 4-9. |
| IEEE | [1] LIN Xin-ping, CAO Shun-hua, and LI Jiong-yi, "Effects of a New Type of Grain Growth Inhibitor on Sintering Behavior of Nanometer Cemented Carbide," Rare Metals and Cemented Carbides, no. 4, pp. 4-9, 2004. keywords: {nanometer cemented carbide;grain growth inhibitor;vacuum sintering;densification;grain growth} |