Research on Causes for Cup-Cone Fractures of Lanthanum-doped Molybdenum Wires AITranslate
Abstract AITranslate
Research is made on the causes of the cup-cone fractures of lanthanum-doped molybdenum wiresduring drawing, based on the observation and analysis of their morphology and hardness. The results show that the residual Fe is an important influence factor leading to the cup-cone fractures of molybdenum wires. The existing form,particle size and the segregation of La2O3 also results in the cup-cone fractures.
KeyWords AITranslate
1马宝平.掺杂方式对Mo-La合金断裂韧性及掺杂粒子显微结构的影响[J].湖南有色金属,2010,26(2):31-33. 被引量：1
2张久兴,周美玲,左铁镛,聂祚仁,胡延槽,王金淑.稀土掺杂钼的强韧化与电子发射性能研究[J].北京工业大学学报,1998,24(3):10-19. 被引量：5
3杨晓青,贺跃辉,罗振中,龙郑易.掺杂La对钼丝组织和性能的影响[J].稀有金属快报,2006,25(3):30-33. 被引量：26
4任宝江,黄晓玲,傅小俊.钼棒在轧制及拉伸过程出现的劈裂、断丝原因分析[J].稀有金属快报,2005,24(1):21-24. 被引量：5
5李大成,卜春阳,赵宝华.钼丝断裂行为研究[J].中国钼业,2003,27(6):37-40. 被引量：3
6张国君,刘刚,孙院军,孙军.氧化镧弥散强化钼合金裂纹扩展的TEM原位观察[J].稀有金属材料与工程,2010,39(5):828-831. 被引量：9
7BeutleyAJ.钼丝断口夹杂物的分析[J].张振兴,译.稀有金属材料与工程,1983,(8):82-83.
8王政伟,贺跃辉,罗振中.掺镧钼烧结裂纹产生原因浅析[J].中国钼业,2011,35(2):42-44. 被引量：3
1李大成,卜春阳,赵宝华,王锦.微掺镧钼丝组织和性能[J].中国钼业,2006,30(1):39-41. 被引量：9
2吴恺威,邓沛然,翟靖,张涛.微孔和杂质对拉制铜线断裂的影响[J].热加工工艺,2016,45(19):259-261. 被引量：1
3王冰.浅谈连续退火拉线中线材质量的控制[J].天津光电线缆技术,2015,0(4):6-8.
4罗锋,余琪,钟方友.大拉铜线拉制过程中断线的原因分析及对策[J].铜业工程,2013(4):19-20. 被引量：1
5哈胜男,任颂赞,谢春生,陈德华,马春霞.200系列不锈钢钢丝失效分析[J].材料开发与应用,2008,23(1):51-54. 被引量：4
6黄素英.端盖拉深工艺与模具设计[J].金属加工：热加工,2012(19):59-60.
7李明茂,汪建华,袁静.超细铜线拉制过程中断线原因分析与对策[J].特种铸造及有色合金,2012,32(6):583-586. 被引量：6
8解兴锋.线切割钼丝拉制影响因素分析[J].硅谷,2012,5(7):111-111.
9曹军,丁雨田,曹文辉.单晶铜键合丝制备过程中的断线研究[J].机械工程学报,2010,46(22):84-89. 被引量：9
10陈锡侯,王梦寒,门正兴,温雪峰.制动梁架整体成形工艺开发与技术实现[J].重庆大学学报：自然科学版,2008,31(11):1247-1250.
Basic Information:
DOI：
Chinese Library Classification Number:TG146.412[金属学及工艺—金属材料]
Citation Information:
Research is made on the causes of the cup-cone fractures of lanthanum-doped molybdenum wiresduring drawing, based on the observation and analysis of their morphology and hardness. The results show that the residual Fe is an important influence factor leading to the cup-cone fractures of molybdenum wires. The existing form,particle size and the segregation of La2O3 also results in the cup-cone fractures.
quote
| GB/T 7714-2015 | [1] WANG Yun-xuan, LI Zhi-xiang. Research on Causes for Cup-Cone Fractures of Lanthanum-doped Molybdenum Wires[J]. Rare Metals and Cemented Carbides, 2013(3): 46-49. |
| MLA | [1] WANG Yun-xuan, and LI Zhi-xiang. "Research on Causes for Cup-Cone Fractures of Lanthanum-doped Molybdenum Wires." Rare Metals and Cemented Carbides, no. 3, 2013, pp. 46-49. |
| APA | [1] WANG Yun-xuan, & LI Zhi-xiang. (2013). Research on Causes for Cup-Cone Fractures of Lanthanum-doped Molybdenum Wires. Rare Metals and Cemented Carbides(3), 46-49. |
| IEEE | [1] WANG Yun-xuan and LI Zhi-xiang, "Research on Causes for Cup-Cone Fractures of Lanthanum-doped Molybdenum Wires," Rare Metals and Cemented Carbides, no. 3, pp. 46-49, 2013. keywords: {lanthanum-doped Mo wire;cup-cone fracture;abnormal microstructure;formation cause} |