Fracture Defects of W-Ni-Cu Alloy and Their Technological Influence Factor Analysis AITranslate
Abstract AITranslate
During the fractography of W-Ni-Cu alloy, various defects such as pore, pollution and ingredient segregation and so on. have been found. This paper analyzes the technological factors causing formation of these defects and gives suggestions for process improvement.
KeyWords AITranslate
1梁容海,王伏生,周载明,易富德,高宏伟.制备W－Ni－Cu钨合金的热解还原法工艺探讨[J].稀有金属与硬质合金,1994,22(3):28-32. 被引量：3
2王伏生,赵慕岳,梁容海,周载明.影响W-Ni-Cu合金材质均匀性的工艺因素研究[J].粉末冶金技术,1993,11(1):37-42. 被引量：8
1刘桂荣,王德文,陈伟.93W-5Ni-2Cu烧结工艺的研究[J].粉末冶金工业,2004,14(4):10-13. 被引量：1
2邹惠兰.钨基重合金的研究与应用现状[J].湖南冶金,1997(2):60-64. 被引量：11
1叶途明,易健宏,李丽娅,彭元东,吕豫湘,胡礼福.高密度钨合金研究的新进展[J].粉末冶金材料科学与工程,2003,8(2):134-140. 被引量：7
2范景莲,刘涛,成会朝.中国钨基合金的进步与发展[J].中国钨业,2009,24(5):99-106. 被引量：16
3蔡万玲,张玉英.由白钨酸氢还原制取超细钨粉的工艺研究[J].中国钨业,2010,25(3):27-29.
4王松,谢明,张吉明,陈宏燕,胡洁琼,杨有才,陈永泰,刘满门,崔浩.W-Re高比重合金的SPS烧结[J].中国钨业,2010,25(6):25-27. 被引量：2
5刘桂荣,王玲,裴燕斌,葛启录.HIP对65WNiCu合金力学性能的影响[J].粉末冶金技术,2011,29(3):210-213. 被引量：2
6王松,陈宏燕,胡洁琼,谢明,杨有才,张吉明,陈永泰,刘满门,崔浩.高比重钨合金的研究现状[J].贵金属,2011,32(3):85-88. 被引量：14
7唐超.钼铜复合材料的发展[J].有色金属与稀土应用,2015,0(2):16-26.
8刘春佳.射线屏蔽用钨合金大制品的微观结构和机械性能研究[J].山西冶金,2018,41(2):45-47.
9刘东光,张力,罗来马.Zr、Ti元素掺杂对高比重W-Cu-Ni/Y_(2)O_(3)复合材料的显微组织和性能的影响规律研究[J].中国钨业,2021,36(1):28-34.
10姚惠龙,熊宁,王玲,秦颖楠,周武平,杨林.循环热处理对93W–5Ni–2Fe高比重钨合金冲击韧性的影响[J].粉末冶金技术,2021,39(3):269-273. 被引量：1
1杨道军.断口缺陷对冲击试验结果的影响和处理[J].锅炉压力容器安全技术,1996(1):23-25.
2胡中伟,魏建国,韩全军.高强船板拉伸试样断口缺陷分析研究[J].宽厚板,2012(3):26-30.
3刘年富.船板拉伸断口缺陷的成因及预防[J].材料开发与应用,2009,24(1):26-29. 被引量：9
4马晓妹,肖洪斌.9Cr2Mo冷轧辊开裂原因分析[J].江西冶金,2004,24(5):23-25. 被引量：1
5邵玉田,王珏.LY12预拉抻厚板中“氧化膜”本质的研究[J].轻金属,1996(1):55-58.
6刘振成,侯基林,曹建刚,姜德刚.SWRH82B硬线尖状断口研究[J].包头钢铁学院学报,2003,22(1):50-53. 被引量：1
7刘守显,李建新,靳芳芳.正火对中厚板偏析断口组织与力学性能的影响[J].金属热处理,2011,36(2):94-96. 被引量：5
8杨慧贤.船板钢拉伸断口分层原因分析及工艺改进[J].钢铁钒钛,2016,37(2):144-148. 被引量：3
9庞钧,侯巧玲,白小明,宋权三,吴逸贵,顾进立,何彦永,陈菁.9Cr2Mo钢冷轧辊断裂分析[J].大型铸锻件,1982(4):141-145.
10庞钧,侯巧玲,白小明.Cr-Ni-Mo铸钢件中的杆状断口[J].大型铸锻件,1981(3):28-35.
Basic Information:
DOI：
Chinese Library Classification Number:TG146.411[金属学及工艺—金属材料];TG111.91[金属学及工艺—物理冶金]
Citation Information:
During the fractography of W-Ni-Cu alloy, various defects such as pore, pollution and ingredient segregation and so on. have been found. This paper analyzes the technological factors causing formation of these defects and gives suggestions for process improvement.
quote
| GB/T 7714-2015 | [1] LI Yi-gui, XIONG Xiang-jun, WANG Fu-sheng. Fracture Defects of W-Ni-Cu Alloy and Their Technological Influence Factor Analysis[J]. Rare Metals and Cemented Carbides, 1995(4): 17-21. |
| MLA | [1] LI Yi-gui, et al., "Fracture Defects of W-Ni-Cu Alloy and Their Technological Influence Factor Analysis." Rare Metals and Cemented Carbides, no. 4, 1995, pp. 17-21. |
| APA | [1] LI Yi-gui, XIONG Xiang-jun, & WANG Fu-sheng. (1995). Fracture Defects of W-Ni-Cu Alloy and Their Technological Influence Factor Analysis. Rare Metals and Cemented Carbides(4), 17-21. |
| IEEE | [1] LI Yi-gui, XIONG Xiang-jun, and WANG Fu-sheng, "Fracture Defects of W-Ni-Cu Alloy and Their Technological Influence Factor Analysis," Rare Metals and Cemented Carbides, no. 4, pp. 17-21, 1995. keywords: {W alloy, fracture defect, technological factor} |