Investigation on Preparation of Coarse Crystal W Powder through Li activated H 2 Reduction of WO 3 AITranslate
Abstract AITranslate
Li activated H 2 reduction of WO 3 is carried out in four steps. During reduction of WO 3 with 200×10 -6 lithia at 900-950℃, the reduction duration can decrease by ～20%,The activation is greatly shown in the step of WO 2 W. The coarsening of W powder size and the effect of Li addition are clearly indicated in the step of WO 2.72 -WO 2,particularly in the step of WO 2-W. The mechanism of activation and grain coarsening during reduction is discussed.
KeyWords AITranslate
1孙宝琦.－[J].稀有金属与硬质合金,1998,(4):1-1.
1吴湘伟,罗劲松,陆必治,谢晨辉,皮志明,胡茂中,徐涛,吴国根,余志明,易丹青.Crystal growth of tungsten during hydrogen reduction of tungsten oxide at high temperature[J].中国有色金属学会会刊：英文版,2009,0(S3):785-789. 被引量：4
2迟静,李惠琪,王淑峰,李敏.矿用WC硬质合金的研究进展与趋势[J].矿山机械,2010,38(8):23-28. 被引量：7
3德志强.高质量结晶钨粉制取的工艺研究[J].硬质合金,2014,31(3):166-172. 被引量：1
1袁明健,顾金宝.氢气脱蜡工艺与原料WC碳量的选择[J].硬质合金,2010,27(5):293-297. 被引量：2
2王明胜,孙东平,欧阳琪.精磨WC-Co矿用齿在水及切削液中的腐蚀行为[J].凿岩机械气动工具,2012,38(2):34-38.
3王梅,姬强,李惠琪,迟静,王淑峰.原位冶金反应粗晶碳化钨复合材料的组织研究[J].材料导报,2012,26(14):47-50. 被引量：1
4迟静,李惠琪,王淑峰,李敏,李建楠,王梅,高旭杰.直流电弧原位冶金制备粗晶碳化钨块体复合材料[J].中国有色金属学报,2013,23(5):1262-1268. 被引量：5
5黄广华,盛银梅,王德志.原位合成WC/W表面复合材料组织和性能研究[J].硬质合金,2018,35(6):420-426. 被引量：1
6王泽宇,王洪福,赵文,王光,王海鹏.TiC/TaC添加剂对WC-Co硬质合金性能改进研究[J].稀有金属与硬质合金,2019,47(1):70-73. 被引量：1
7张勇,张国华.纳米钨辅助氢气还原氧化钨制备超细钨粉[J].粉末冶金材料科学与工程,2020,25(5):375-380. 被引量：2
8陈杉杉.还原钨粉粒度特性的过程研究[J].粉末冶金材料科学与工程,2020,25(5):389-395. 被引量：3
9龙本夫,林高安,张太全,沈思奇.APT煅烧工艺对WO_(2.72)晶体生长机制的影响[J].粉末冶金材料科学与工程,2021,26(1):32-39.
10李哲雨,李尚杰,李必红,王峰,同剑,苏红辈.钨粉颗粒形貌对钨铜合金药型罩破甲性能的影响[J].工程爆破,2021,27(4):94-99. 被引量：1
1莫玉琛,罗振中.结晶钨粉的研制[J].稀有金属与硬质合金,1994,22(4):1-3. 被引量：2
2莫玉琛,罗振中.结晶钨粉的研制[J].四川有色金属,1994(4):5-7. 被引量：2
3德志强.高质量结晶钨粉制取的工艺研究[J].硬质合金,2014,31(3):166-172. 被引量：1
4张文朴.钨钼基础工业化学(十)[J].中国钨业,1997,0(12):21-27.
5朱旺喜.外刊科技文摘[J].中国钨业,1996,0(8):34-35.
6吴恩熙,钱崇梁,张卫兵.钨─钴混合氧化物直接气相还原／碳化相变过程[J].中南工业大学学报,1996,27(3):303-307.
7孙宝琦,吴国龙,陈一鸣.三氧化钨氢还原时碱金属元素引起的钨粉超常规粗化现象[J].稀有金属与硬质合金,1998,26(4):1-6. 被引量：4
8杉泽泰次郎,吴继宝.钨基烧结材料的制造方法[J].中国钨业,1990(11):27-31.
9付绸琳,钟雄,付高明.仙人岩地表金矿石氰化浸出试验[J].有色金属：冶炼部分,2013(6):37-39. 被引量：8
10蒋显亮,M.BOULOS.Induction plasma spheroidization of tungsten and molybdenum powders[J].中国有色金属学会会刊：英文版,2006,16(1):13-17. 被引量：28
Basic Information:
DOI：
Chinese Library Classification Number:TF123.24[冶金工程—粉末冶金]
Citation Information:
Li activated H 2 reduction of WO 3 is carried out in four steps. During reduction of WO 3 with 200×10 -6 lithia at 900-950℃, the reduction duration can decrease by ～20%,The activation is greatly shown in the step of WO 2 W. The coarsening of W powder size and the effect of Li addition are clearly indicated in the step of WO 2.72 -WO 2,particularly in the step of WO 2-W. The mechanism of activation and grain coarsening during reduction is discussed.
quote
| GB/T 7714-2015 | [1] SUN Bao-qi, CHEN Yi-ming. Investigation on Preparation of Coarse Crystal W Powder through Li activated H 2 Reduction of WO 3[J]. Rare Metals and Cemented Carbides, 1999(1): 1-6. |
| MLA | [1] SUN Bao-qi, and CHEN Yi-ming. "Investigation on Preparation of Coarse Crystal W Powder through Li activated H 2 Reduction of WO 3." Rare Metals and Cemented Carbides, no. 1, 1999, pp. 1-6. |
| APA | [1] SUN Bao-qi, & CHEN Yi-ming. (1999). Investigation on Preparation of Coarse Crystal W Powder through Li activated H 2 Reduction of WO 3. Rare Metals and Cemented Carbides(1), 1-6. |
| IEEE | [1] SUN Bao-qi and CHEN Yi-ming, "Investigation on Preparation of Coarse Crystal W Powder through Li activated H 2 Reduction of WO 3," Rare Metals and Cemented Carbides, no. 1, pp. 1-6, 1999. keywords: {Li, reduction, activation, crystalline W powder} |