Experimental Study on Preparation of ScB_2 by Carbon Thermal Reduction AITranslate
Abstract AITranslate
ScB2was prepared by carbon thermal reduction in vacuum at high temperature with Sc2O3,B4 C and C powder as the raw materials.Qualitative and quantitative analysis was made of product phase composition by XRD and Rietveld whole pattern fitting.The results show that ScB2 synthesis rate can be more than 99% by carbon thermal reduction with Sc2O3 and B4C as the raw materials and appropriate amount of C powder as the reactive agent.
KeyWords AITranslate
1周身林.多晶稀土六硼化物阴极的制备、结构与性能研究[D].北京工业大学2011
2G. Levchenko,A. Lyashchenko,V. Baumer,A. Evdokimova,V. Filippov,Yu. Paderno,N. Shitsevalova.Preparation and some properties of ScB 2 single crystals[J]. Journal of Solid State Chemistry . 2006 (9)
3G. Balakrishnan,M.R. Lees,D.M c K. Paul.Growth of large single crystals of rare earth hexaborides[J]. Journal of Crystal Growth . 2003 (1)
4S. P. Gordienko,G. N. Makarenko,V. B. Fedorus,I. I. Timoveeva,K. F. Chernysheva,E. V. Marek.Interaction of boron carbide with scandium oxide[J]. Powder Metallurgy and Metal Ceramics . 1995 (7)
1曹佳伟,周夏芝,嵇友迪,葛谣,范佳俊,周钰康,彭银仙.稀土元素冶金技术研究进展[J].广州化工,2018,46(4):17-18. 被引量：1
1杨亚,欧梅桂,胡燕燕,罗定生,李仲卿,王涛.离子掺杂对纳米氧化钆发光强度及驰豫性能的影响[J].化工新型材料,2019,47(8):237-240.
1龙郑易,张腾辉,王庆,王平江.Rietveld全谱拟合在水雾化FeNi30触媒粉末物相分析及氧含量测定中的应用[J].粉末冶金材料科学与工程,2012,17(2):247-251. 被引量：1
2韩海波,陈虹锦,钱雪峰,宰建陶.TiO_2粉末多晶X射线衍射Rietveld全谱拟合定量相分析[J].实验室研究与探索,2011,30(12):34-37. 被引量：5
3邓磊,蔡攀,杜娟.Rietveld全谱拟合法计算水泥熟料中方镁石的含量[J].水泥,2015(11):56-58. 被引量：2
4张智力,刘丞,许超,姜传兴,陈淑祥.玻璃容器内表面纤维状物质成分的分析研究[J].硅酸盐通报,2014,33(2):431-435.
5倪玉华,马礼敦,沈孝良,施国顺.Rietveld全谱拟合表征掺杂ZnO陶瓷[J].高等学校化学学报,2000,21(5):785-788. 被引量：7
6吴限,徐维泽,张宇佳,马诚,李丽华,张金生.ZnO/CeO_2复合纳米材料的Rietveld全谱拟合物相表征[J].石油化工高等学校学报,2017,30(1):14-17. 被引量：5
7丁浩.石灰石和熟料混合挤压后在不同粒级段组成比例的研究[J].中国水泥,2016(12):73-75.
8刘齐文,陈常连,陈斐,沈强,张联盟.CaO稳定ZrO_2陶瓷Rietveld定量相分析[J].武汉理工大学学报,2010,32(8):13-17. 被引量：1
9谢萍,刘亚平,韩大川.工业糠醛定性与定量分析[J].检验检疫科学,2000,10(5):7-8. 被引量：1
10许聚良,李亚伟,陈汀水.Rietveld全谱拟合法测定莫来石固溶体含量[J].耐火材料,2009,43(4):303-305. 被引量：1
Basic Information:
DOI：
Chinese Library Classification Number:TQ133.21[化学工程—无机化工]
Citation Information:
ScB2was prepared by carbon thermal reduction in vacuum at high temperature with Sc2O3,B4 C and C powder as the raw materials.Qualitative and quantitative analysis was made of product phase composition by XRD and Rietveld whole pattern fitting.The results show that ScB2 synthesis rate can be more than 99% by carbon thermal reduction with Sc2O3 and B4C as the raw materials and appropriate amount of C powder as the reactive agent.
quote
| GB/T 7714-2015 | [1] LIU Hua, SONG Jue-min, CHENG Yong, et al. Experimental Study on Preparation of ScB_2 by Carbon Thermal Reduction[J]. Rare Metals and Cemented Carbides, 2015(5): 9-11. |
| MLA | [1] LIU Hua, et al., "Experimental Study on Preparation of ScB_2 by Carbon Thermal Reduction." Rare Metals and Cemented Carbides, no. 5, 2015, pp. 9-11. |
| APA | [1] LIU Hua, SONG Jue-min, CHENG Yong, ZHU Jian-jun, & PANG Ying. (2015). Experimental Study on Preparation of ScB_2 by Carbon Thermal Reduction. Rare Metals and Cemented Carbides(5), 9-11. |
| IEEE | [1] LIU Hua, SONG Jue-min, CHENG Yong, ZHU Jian-jun, and PANG Ying, "Experimental Study on Preparation of ScB_2 by Carbon Thermal Reduction," Rare Metals and Cemented Carbides, no. 5, pp. 9-11, 2015. keywords: {ScB2;Sc2O3;B4C;C powder;carbon thermal reduction} |