Study of Hot Pressed Micro--crystalline Boron Carbide AITranslate
Abstract AITranslate
Study is made of hot pressing of micro--crys talline boron carbide from ultra--fine boron carbide. The grain size, porosity, transverse s trength, fracture morphology and I notion factor of the ma tenalis also investigated. The relationship between transverse strength andgrain size is expressed' as follows: a￣387. 6+ 182. 3 1The friction factor of boron carbide is determined as: K￣0. 093.
KeyWords AITranslate
1吴芳,吕军.碳化硼陶瓷的制备及应用[J].五邑大学学报：自然科学版,2002,16(1):45-49. 被引量：12
1章晓波,刘宁.碳化硼材料的性能、制备与应用[J].硬质合金,2006,23(2):120-125. 被引量：34
2裴立宅.碳化硼材料的制备技术[J].佛山陶瓷,2007,17(4):37-41. 被引量：6
3王正军.碳化硼抗弹陶瓷研究进展[J].硅酸盐通报,2008,27(1):132-135. 被引量：6
4王正军.碳化硼抗弹陶瓷的制备方法及应用[J].中国粉体技术,2008,14(3):56-59. 被引量：10
5徐璟玉,吴文远,边雪,涂赣峰.原位生成CeB_6/B_4C陶瓷的力学性能和显微组织[J].功能材料,2009,40(2):278-280. 被引量：3
6王国亮,蔡星会,姬国勋,卢江仁.B_4C陶瓷摩擦学性能研究现状与分析[J].材料导报,2012,26(7):45-48. 被引量：1
7董云娜.蓝宝石晶片粗磨工艺的研究[J].金刚石与磨料磨具工程,2017,37(3):88-90. 被引量：3
8郭在在,曹剑武,燕东明,赵斌,贾书波,李国斌,傅宇东.碳化硼陶瓷粉体制备研究进展[J].兵器装备工程学报,2017,38(12):278-280. 被引量：4
9赵兴国,聂慧慧,陈洪胜,张媛琦.B_4C/AZ91镁基复合材料的微观组织及力学性能研究[J].铸造设备与工艺,2018(5):57-62. 被引量：1
10董开朝,高帅波,崔晓华,李盼,李欣,王帅,姜胜南,魏冬卉,邢鹏飞.烧结气氛对碳化硼水选废料制备耐火材料性能的影响[J].耐火材料,2018,52(6):438-441.
1曹仲文.碳化硼材料在核反应堆中的应用与发展[J].辽宁化工,2006,35(7):399-400. 被引量：16
2硼化物文摘[J].无机盐技术,2007(4):40-40.
3曹仲文.制备核工业用碳化硼材料的工艺探讨[J].机械工程师,2006(6):57-58. 被引量：2
4王凤娥（摘译）.改良的碳化硼成形工艺可制备更好的防弹衣[J].现代材料动态,2006(7):9-10.
5丁硕,温广武,雷廷权.碳化硼材料研究进展[J].材料科学与工艺,2003,11(1):101-105. 被引量：38
6曹仲文,张继红.核工业用碳化硼材料产业化前景分析[J].新材料产业,2006(5):59-61. 被引量：7
7吴芳,王零森.热压碳化硼材料的纳米摩擦性能研究[J].粉末冶金材料科学与工程,2002,7(4):259-264. 被引量：2
8彭可武,马贺利,陈韧,郑溪娟,李猛,涂赣峰.多孔碳化硼的力学性能及其微观组织[J].有色矿冶,2010,26(2):32-34. 被引量：2
9王零森,吴芳.碳化硼陶瓷磨损特性的点接触显微镜研究[J].粉末冶金材料科学与工程,2002,7(3):165-169.
10吴思远,李鹏程,杨雪萍,吴守军.烧结温度和保温时间对AlB_2合成反应的探析[J].黑龙江科技信息,2014(9):80-80.
Basic Information:
DOI：
Chinese Library Classification Number:TQ127.12[化学工程—无机化工]
Citation Information:
Study is made of hot pressing of micro--crys talline boron carbide from ultra--fine boron carbide. The grain size, porosity, transverse s trength, fracture morphology and I notion factor of the ma tenalis also investigated. The relationship between transverse strength andgrain size is expressed' as follows: a￣387. 6+ 182. 3 1The friction factor of boron carbide is determined as: K￣0. 093.
quote
| GB/T 7714-2015 | [1] ZHOU Rong-xing, WANG Ling-sen, DENG Ke-qin, et al. Study of Hot Pressed Micro--crystalline Boron Carbide[J]. Rare Metals and Cemented Carbides, 1994(2): 16-20. |
| MLA | [1] ZHOU Rong-xing, et al., "Study of Hot Pressed Micro--crystalline Boron Carbide." Rare Metals and Cemented Carbides, no. 2, 1994, pp. 16-20. |
| APA | [1] ZHOU Rong-xing, WANG Ling-sen, DENG Ke-qin, & YANG Ju-mei. (1994). Study of Hot Pressed Micro--crystalline Boron Carbide. Rare Metals and Cemented Carbides(2), 16-20. |
| IEEE | [1] ZHOU Rong-xing, WANG Ling-sen, DENG Ke-qin, and YANG Ju-mei, "Study of Hot Pressed Micro--crystalline Boron Carbide," Rare Metals and Cemented Carbides, no. 2, pp. 16-20, 1994. keywords: {hot pressing, micro crystalline, boron carbide} |