Effects of Sintering Process on the Service Life of the D152mm YG6 Double-faced Anvils AITranslate
Abstract AITranslate
Impact of sintering temperature and time on the axial density distribution,microstructure,hardness and bending strength of D152 mm YG6 cemented carbide double-faced anvils were studied by drainage method,SEM,EDS and three point bending.The service life of the double-faced anvil was tested by experiment.The results show that the D152 mm double-faced anvil,prepared by vacuum sintering at 1 390 ℃ for 6 h with YG6 alloy,has fine WC grains,low grain adjacency degree between WC and WC,and an average service life of 2 408 times.
KeyWords AITranslate
1邹仿棱.国内外顶锤生产技术状况及发展方向[J].世界有色金属,1999(12):7-8. 被引量：1
2王民,王松顺.硬质合金顶锤和压缸的破裂特征、破坏因素的分析和提高使用寿命的途径[J].硬质合金,1994,11(4):231-240. 被引量：13
3唐群,呼文贤,彭刚,汪有明.进口硬质合金顶锤和压缸的解剖分析[J].粉末冶金技术,1996,14(1):44-51. 被引量：5
1秦琴,孙卫鹏,栾道成,王正云.烧结温度对超细YG6硬质合金性能的影响[J].热加工工艺,2016,45(18):77-79. 被引量：3
2一种耐磨耐腐蚀硬质合金材料[J].中国钨业,2003,18(1):44-44.
3张科元,查健中.新型热作模具钢H13Ni3Al的研究[J].南方金属,2009(3):1-4. 被引量：1
4董洪峰,郭从盛,张锋刚.添加氧化镧WC-11Co-2.1TaC硬质合金的组织及性能[J].陕西理工学院学报：自然科学版,2016,32(5):1-5. 被引量：2
5王崇琳.烧结体密度的精确测定[J].粉末冶金技术,1989,7(1):43-44. 被引量：4
6阳建宏.YG6长条薄片弯曲变形影响因素的探讨[J].硬质合金,2002,19(2):87-90. 被引量：5
7曹明明,张建良,邢相栋,文永才,王春龙.钒钛磁铁矿含碳球团直接还原研究[J].钢铁钒钛,2012,33(4):28-33. 被引量：6
8章晓辉,马觉.氧化铁粉质量的影响因素分析及解决措施[J].中国冶金,2007,17(8):17-19. 被引量：2
9陈伟鹏,李光卫,赵增武,李保卫,武文斐.褐铁矿的煤泥球团直接还原[J].过程工程学报,2015,15(6):1029-1033. 被引量：1
10王云,朱荣,郭亚光,周萌,郭明威,周春芳.铜渣还原磁选工艺实验研究[J].有色金属科学与工程,2014,5(5):61-67. 被引量：15
Basic Information:
DOI：
Chinese Library Classification Number:TF124.53[冶金工程—粉末冶金]
Citation Information:
Impact of sintering temperature and time on the axial density distribution,microstructure,hardness and bending strength of D152 mm YG6 cemented carbide double-faced anvils were studied by drainage method,SEM,EDS and three point bending.The service life of the double-faced anvil was tested by experiment.The results show that the D152 mm double-faced anvil,prepared by vacuum sintering at 1 390 ℃ for 6 h with YG6 alloy,has fine WC grains,low grain adjacency degree between WC and WC,and an average service life of 2 408 times.
quote
| GB/T 7714-2015 | [1] LI Xian-rong, YANG Shao-qing, XU Jun, et al. Effects of Sintering Process on the Service Life of the D152mm YG6 Double-faced Anvils[J]. Rare Metals and Cemented Carbides, 2010(4): 37-39. |
| MLA | [1] LI Xian-rong, et al., "Effects of Sintering Process on the Service Life of the D152mm YG6 Double-faced Anvils." Rare Metals and Cemented Carbides, no. 4, 2010, pp. 37-39. |
| APA | [1] LI Xian-rong, YANG Shao-qing, XU Jun, & LI Qiang. (2010). Effects of Sintering Process on the Service Life of the D152mm YG6 Double-faced Anvils. Rare Metals and Cemented Carbides(4), 37-39. |
| IEEE | [1] LI Xian-rong, YANG Shao-qing, XU Jun, and LI Qiang, "Effects of Sintering Process on the Service Life of the D152mm YG6 Double-faced Anvils," Rare Metals and Cemented Carbides, no. 4, pp. 37-39, 2010. keywords: {YG6 double-faced anvils;cold isostatic pressing;sintering temperature;heat preservation time;operating life} |