Effect of Carbon Content on Microstructure and Properties of Ultrafine WC-12%Co Cemented Carbides AITranslate
Abstract AITranslate
Eight groups of WC-12%Co cemented carbides with different carbon contents were prepared by mixing,pressing,and hot isostatic pressing sintering.The influences of carbon content on the microstructure and mechanical properties of the cemented carbides were analyzed using metallographic microscope,scanning electron microscope,hardness tester,and electromechanical universal test machine.The results show that the WC-12%Co cemented carbides with carbon contents of 5.26%~5.42%are in the WC+γtwo-phase zone.When the carbon content is less than or equal to 5.22%,the cemented carbide exhibits flocculent and needle like decarburization phases.When the carbon content is greater than or equal to 5.46%,black flocculent carburized phase appears in the cemented carbides,accompanied by the appearance and aggregation of coarse grains and the segregation of cobalt.As the carbon content gradually increases,the WC grains gradually grow larger,the crystallization tends to be complete,the grain edges tend to be straight,and the grain boundaries become clearer.When the carbon content reaches 5.54%,rounded corners appear at the edges of the WC grains.The cemented carbides with carbon contents of 5.26%~5.42%are in WC and Co two-phase zone,exhibiting superior comprehensive mechanical properties,with hardness maintained at 1777~1695 kg/mm2 and bending strength of 3357~3290 MPa.
KeyWords AITranslate
1曾瑞霖,李剑峰,马赛,龙宁华,张湘,吴育藩.WC粉末特性对PCB用超细晶硬质合金棒材微观组织结构和性能的影响[J].硬质合金,2022,39(6):454-460. 被引量：3
2杨树忠,王玉香,肖颖奕,张帆,许洋.超细晶WC-Co硬质合金制备工艺研究[J].世界有色金属,2019,44(22):142-144. 被引量：3
3刘斌,孔德方,戴炳蔚.两步烧结对超细晶WC-4%Co硬质合金微观组织及性能的影响[J].硬质合金,2019,36(6):406-413. 被引量：1
4李雨衡,刘雪梅,刘超,吕皓,宋晓艳.VC和碳含量对超细晶硬质合金室温和高温性能的影响[J].稀有金属材料与工程,2021,50(6):2169-2176. 被引量：5
5张璐,李剑峰,尹运春,刘渊溢,陆必志.WC粉末特性对超细晶硬质合金烧结敏感性影响的研究[J].硬质合金,2020,37(1):51-59. 被引量：10
6黄田贞,吴恩熙,李詠侠,邹丹,谢元彦.碳含量对WC-6Co超细晶硬质合金WC晶粒长大激活能的影响[J].稀有金属与硬质合金,2017,45(5):57-62. 被引量：4
7胡启明,廖宇.贫碳WC-12%(Co+Ni)硬质合金微观组织与性能[J].硬质合金,2023,40(1):66-72. 被引量：1
8唐彦渊,钟志强,羊求民,王红云,徐国钻.碳含量对WC-10Co硬质合金微观组织及力学性能的影响[J].稀有金属与硬质合金,2021,49(6):73-78. 被引量：8
9李敏,甘绪发,张洪刚.碳含量对WC-5.7%Co-5.7%Ni-0.13%Cr硬质合金组织与性能的影响[J].稀有金属与硬质合金,2022,50(3):87-92. 被引量：5
10顾金宝,刁椿珉,时凯华,董定乾,曾伟,董凯林,向新.碳含量对非均匀硬质合金组织和性能的影响[J].硬质合金,2021,38(3):193-200. 被引量：4
1提高硬质合金抗氧化磨损性能取得进展[J].工具展望,2024(1):24-24.
2唐彦渊,羊求民,徐国钻,王红云,钟志强.微量Y_(2)O_(3)对WC−6Co非均匀结构硬质合金微观结构及性能的影响[J].粉末冶金技术,2024,42(2):184-191.
3刘涛,支中正,王英杰,李富平,周付超,康健,何志敏.LncRNA GAS5通过miR-21调控脊髓损伤后神经细胞凋亡的机制研究[J].骨科,2024,15(2):145-154.
4周猛兵,张超,魏连峰,陈高詹.锆合金电子束熔丝增材组织与性能研究[J].焊接技术,2024,53(3):1-6.
5董福宇,关金源,张悦,申向阳,郭子鹤,黄宏军,袁晓光.高温变形对Al_(0.1)(MoNbTa_(0.7)ZrTi)难熔高熵合金微观组织的影响[J].特种铸造及有色合金,2024,44(3):294-298.
6程宗辉,陈云鹏,舒送,蔡绪康,王磊磊.激光熔化沉积钛合金-高熵合金梯度材料组织演变研究[J].精密成形工程,2024,16(4):129-137.
7张钱伟,廖军,叶潇潇,叶红云,张玉琪,董凯林.Cr_(3)C_(2)和VC复合抑制剂对超细WC-9%Co硬质合金制备及性能的影响[J].中国钨业,2023,38(6):47-52.
8陈庆强,马冠杰,孙捷,孙幸子,于亚磊,李顺龙.时效析出强化对GW83镁合金摩擦磨损行为的影响[J].材料工程,2024,52(4):127-137.
9鲁飞,刘树峰,许亿,李慧,张帅,温永清.铈添加对Al-Mn靶材物相转变及应用性能的影响[J].中国稀土学报,2024,42(2):330-338.
Basic Information:
DOI：
Chinese Library Classification Number:TG135.5[一般工业技术—材料科学与工程]
Citation Information:
Eight groups of WC-12%Co cemented carbides with different carbon contents were prepared by mixing,pressing,and hot isostatic pressing sintering.The influences of carbon content on the microstructure and mechanical properties of the cemented carbides were analyzed using metallographic microscope,scanning electron microscope,hardness tester,and electromechanical universal test machine.The results show that the WC-12%Co cemented carbides with carbon contents of 5.26%~5.42%are in the WC+γtwo-phase zone.When the carbon content is less than or equal to 5.22%,the cemented carbide exhibits flocculent and needle like decarburization phases.When the carbon content is greater than or equal to 5.46%,black flocculent carburized phase appears in the cemented carbides,accompanied by the appearance and aggregation of coarse grains and the segregation of cobalt.As the carbon content gradually increases,the WC grains gradually grow larger,the crystallization tends to be complete,the grain edges tend to be straight,and the grain boundaries become clearer.When the carbon content reaches 5.54%,rounded corners appear at the edges of the WC grains.The cemented carbides with carbon contents of 5.26%~5.42%are in WC and Co two-phase zone,exhibiting superior comprehensive mechanical properties,with hardness maintained at 1777~1695 kg/mm2 and bending strength of 3357~3290 MPa.
quote
| GB/T 7714-2015 | [1] FU Sheng-hua, XIAO Sen, CHEN Wei-cai, et al. Effect of Carbon Content on Microstructure and Properties of Ultrafine WC-12%Co Cemented Carbides[J]. Rare Metals and Cemented Carbides, 2024(2): 63-69. |
| MLA | [1] FU Sheng-hua, et al., "Effect of Carbon Content on Microstructure and Properties of Ultrafine WC-12%Co Cemented Carbides." Rare Metals and Cemented Carbides, no. 2, 2024, pp. 63-69. |
| APA | [1] FU Sheng-hua, XIAO Sen, CHEN Wei-cai, LIU Xin, ZHONG Zhi-qiang, & HUANG Yun-fei. (2024). Effect of Carbon Content on Microstructure and Properties of Ultrafine WC-12%Co Cemented Carbides. Rare Metals and Cemented Carbides(2), 63-69. |
| IEEE | [1] FU Sheng-hua, XIAO Sen, CHEN Wei-cai, LIU Xin, ZHONG Zhi-qiang, and HUANG Yun-fei, "Effect of Carbon Content on Microstructure and Properties of Ultrafine WC-12%Co Cemented Carbides," Rare Metals and Cemented Carbides, no. 2, pp. 63-69, 2024. keywords: {carbon content;ultrafine cemented carbide;WC-12%Co;microstructure;mechanical property} |