Abstract AITranslate
The dehydration process of LaCl3 · 7H2 O at different heating rates in different atmospheres was studied by thermal analyzer. The results show that the dehydration process at 10 ℃/min heating rate in air atmosphere is divided into three stages：42.0-119.2 ℃ ,119.2-174.7 ℃ and 174.7-218.4 ℃ with crys- tal water loss of 2 molecules,4 molecules and 1 molecule,respectively. The dehydration process at 10 ℃/ min heating rate in CO2 atmosphere is also divided into three stages：38.3-109.9 ℃ ,109.9-161.2 ℃ and 161.2-196.2 ℃ with crystal water loss of 3 molecules,3 molecules and 1 molecule,respectively. Both rap- id temperature rise and increased oxidation of the reaction atmosphere are beneficial to the dehydration process of LaCl3 · 7H2O.
KeyWords AITranslate
1成维,黄美松,王志坚,贾帅广,杨露辉.金属镧的制备方法及应用研究现状[J].稀有金属与硬质合金,2014,42(1):62-65. 被引量：7
2陈阳国,方正,唐爱东.LaCl_3·7H_2O晶体的热分解[J].稀土,2002,23(1):56-58. 被引量：8
3耿政松,张琳,谢建军.水合氯化镧LaCl_3·7H_2O的热脱水分析研究[J].同济大学学报：自然科学版,2005,33(12):1704-1706. 被引量：2
1姚飞,马壮,邓雷,乐俊,王燕雯.升温速率在DSC测试中的影响[J].科技经济导刊,2018(12):50-50. 被引量：2
2刘阳,李婕,武震,赵庄,何兰.多种手段测定来氟米特含量研究[J].化学教育（中英文）,2018,39(10):33-35. 被引量：1
3刘新,刘霞,王爱萍,龚维,姚旭霞,吕辉.水中亚硝酸根离子标准物质的研制[J].化学分析计量,2018,27(5):6-10. 被引量：5
4张青海,李云龙,汪扬涛,曾安蓉,林松柏.FAB-La配合物的绿色合成及其对SBR的硫化促进作用研究[J].现代化工,2017,37(9):99-101.
5熊亚选,王振宇,徐鹏,吴玉庭,丁玉龙,马重芳.添加纳米SiO_2对单组分及二元硝酸盐热物性的影响[J].化工学报,2018,69(10):4418-4426. 被引量：7
6刘秀状,黄小凤,马丽萍,尚志标,赵丹,范莹莹,刘红盼.MgO对黄磷炉渣微晶玻璃析晶影响[J].硅酸盐通报,2018,37(8):2606-2609. 被引量：2
7侯聪花,郭晨,刘志强,贾新磊,张诗敏.非溶剂体系温度对细化RDX影响的分子动力学模拟及实验研究[J].火炸药学报,2018,41(4):375-381. 被引量：2
8张磊,范亚蕾,黄月霞,王德强.Ba^(2+),Al^(3+),Sr^(2+)掺杂YF_3∶Ho^(3+),Yb^(3+)上转换发光的研究[J].人工晶体学报,2018,47(5):885-893. 被引量：1
9许永,张叶龙,赵伟杰,王敏,翁立奎,冷光辉,丁玉龙.中高温复合相变储热材料的制备及性能研究[J].无机盐工业,2018,50(5):36-39. 被引量：5
10王继群,张雷,刘丽敏,张雨晴,艾莉蒳,李婧.多核铜槲皮素配合物的制备及抗肿瘤活性测试[J].山东化工,2018,47(19):18-20. 被引量：5
Basic Information:
DOI：
Chinese Library Classification Number:O614.331[理学—无机化学]
Citation Information:
The dehydration process of LaCl3 · 7H2 O at different heating rates in different atmospheres was studied by thermal analyzer. The results show that the dehydration process at 10 ℃/min heating rate in air atmosphere is divided into three stages：42.0-119.2 ℃ ,119.2-174.7 ℃ and 174.7-218.4 ℃ with crys- tal water loss of 2 molecules,4 molecules and 1 molecule,respectively. The dehydration process at 10 ℃/ min heating rate in CO2 atmosphere is also divided into three stages：38.3-109.9 ℃ ,109.9-161.2 ℃ and 161.2-196.2 ℃ with crystal water loss of 3 molecules,3 molecules and 1 molecule,respectively. Both rap- id temperature rise and increased oxidation of the reaction atmosphere are beneficial to the dehydration process of LaCl3 · 7H2O.
quote
| GB/T 7714-2015 | [1] WU Yong-fu, XUE Kai, LIU Zhong-xing, et al. Study on Dehydration Process of LaCl_3·7H_2O[J]. Rare Metals and Cemented Carbides, 2018(5): 46-49. |
| MLA | [1] WU Yong-fu, et al., "Study on Dehydration Process of LaCl_3·7H_2O." Rare Metals and Cemented Carbides, no. 5, 2018, pp. 46-49. |
| APA | [1] WU Yong-fu, XUE Kai, LIU Zhong-xing, WU Wen-yuan, & BIAN Xue. (2018). Study on Dehydration Process of LaCl_3·7H_2O. Rare Metals and Cemented Carbides(5), 46-49. |
| IEEE | [1] WU Yong-fu, XUE Kai, LIU Zhong-xing, WU Wen-yuan, and BIAN Xue, "Study on Dehydration Process of LaCl_3·7H_2O," Rare Metals and Cemented Carbides, no. 5, pp. 46-49, 2018. keywords: {LaCl3 · 7H2O;dehydration;analysis;thermogravimetry （TG）;differential scanning calorimetry（DSC）;differential thermal analysis （DTA）} |