Study on the Efficacy Loss of the La0.75Mg0.25Ni3.47Co0.2Al0.03 Hydrogen Storage Alloy Electrode AITranslate

School of Quality and Technical Supervision of Hebei University;School of Quality and Technical Supervision of Hebei University;School of Quality and Technical Supervision of Hebei University;School of Quality and Technical Supervision of Hebei University;School of Quality and Technical Supervision of Hebei University;School of Quality and Technical Supervision of Hebei University
AITranslate
Publisher: Editorial Office of Rare Metals and Cemented Carbides
Share Citation Information Add to Favorites

    Scan to share on WeChat or Moments

Use WeChat scan.
Share with WeChat friends or Moments

Abstract AITranslate

La0.75Mg0.25Ni3.47Co0.2Al0.03 alloy was prepared by intermediate-frequency induction vacuum melting. The reasons for the efficacy loss of the alloy electrode were investigated by electrochemical and gaseous cycle experiments,SEM and XPS. The results show that capacity attenuation in both discharge and hydrogen absorption cycles takes place in rapid and slow stages. With cycling number increasing,the corrosive oxide on the surface of alloy particle increases during electrochemical cycling, and the contact resistance and charge transfer resistance first decrease and then increase. During gaseous hydrogen absorption and desorp- tion cycling,the crack of the alloy particle increases and the split extent enlarges. The main reason of the alloy electrode capacity decay is the oxidation and corrosion of La and Mg. Alloy particle pulverization ac- celerates the corrosion of La and Mg, and further deteriorates the cycling performance of the alloy electrode.

KeyWords AITranslate

La0.75Mg0.25Ni3.47Co0.2Al0.03 hydrogen storage alloy electrochemical cycle gaseous hydrogen ab- sorption and desorption cycle oxidation corrosion pulverization

1Wei X D, Liu S S, Dong H, et al. Microstructures and electrochemical properties of Co-free ABs-type hydrogen storage alloys through substitution of Ni by Fe[J]. 2007,52(7) :2 423-2 428.

2Dong X P, Lu F X, Yang LY, et al. Influence of spark plasma sintering temperature on electrochemical per- formance of La0.80 Mg0.20 Ni3.75 alloy[J]. Materials Chemistry and Physics, 2008,112(2) : 596-602.

3Dong X P,Zhang YH, LF X,et al. Investigation on microstructures and electrochemical performances of La0.75 Mg0.25 Ni3.5 Cox (x = 0 - 0. 6 ) hydrogen storage alloys [J].Int J Hydrogen Energy, 2007, 32 (18): 4 949- 4 956.

4Liu Y F,Pan H G,Gao M X,etal. Function of A1 on the cycling behavior of the La-Mg-Ni-Co type alloy electrodes[J].Int J Hydrogen Energy, 2008, 33 ( 1 ): 124 - 133.

5Zhu H Y,Wu J,Wang Q D. Disproportionation of LaNi5 and TiFe in 4 MPa H2 at 300 ℃[J]. J Alloys Compd, 1992,185(1) :1-6.

6Inui H,Yamamoto T, Hirota M,et al. Lattice defects in- troduced during hydrogen absorption-desorption cycles and their effects on P-C characteristics in some intermetallic compounds[J]. J Alloys Compd,2002,330-332 :117 -124.

7Evgenij B, Macdonald J R. Impedance spectrocopy theory,experiment and application(2nd edition)[M]. New Jersey:John Wiley & Sons Incorporation,2005. 213.

8Goo N H,Jeomg W T,Lee K S. Effects of Zr addition on discharge properties of mechanically alloyed Mg2 Ni hy drogen-storage alloy electrode[J].J Power Sources, 2000,87 (1-2) : 118-124.

9Nordlien J H,Ono S, Masuko N,et al. Morphology and structure of oxide films formed on magnesium by expo- sure to air and water[J].J Electrochemical Society, 1995,142(10):3 320-3 322.

10Ao B Y,Chen S X,Jiang G Q. A study on wall stress induced by LaNi5 alloy hydrogen absorption-desorption cycles[J].J Alloys Compd,2005,390(1-2) ;122-126.

1董小平,庞艳荣,王芳,杨丽颖.储氢合金吸放氢粉化的声发射原位检测进展[J].电池,2013,43(1):51-53.

2张翰威,李一鸣,任慧平,刘卓承.La_(0.88)Mg_(0.12)Ni_(3.45)与商用AB_5型储氢合金失效行为的对比研究[J].稀土,2016,37(2):21-30. 被引量:3

3郭淼,苑慧萍,刘彧儒,蒋利军.AB3.3~3.7型La-Y-Ni稀土储氢合金微观结构和电化学性能研究[J].稀有金属,2023,47(2):210-217. 被引量:1

1丰洪微,刘向东,吕凯,徐国庆,张皓志.储氢合金电极材料混合处理装置的研究与验证[J].铸造技术,2017,38(6):1292-1294.

2董振伟,王云克,钞春英,马榕彬,武玺旺,高远浩.LaNi_(2.5)Co_(0.5)储氢合金在充放电循环过程中的电化学性能研究[J].信阳师范学院学报:自然科学版,2019,32(1):107-112. 被引量:2

3徐津,闫慧忠,王利,李宝犬,熊玮,张旭.La-Y-Ni系储氢合金材料的研究进展[J].稀土,2020,41(5):114-122. 被引量:8

4郑波,刘雯雯,任权兵,赖华生,冯兰,皮雄,李荣华,钟鸣,林昊.不同Mn含量对A_(2)B_(7)型La-Y-Ni储氢合金性能的影响[J].有色金属:冶炼部分,2023(8):82-88.

1赵一生.焊接热模拟线能量对含稀土硼钢组织和韧性的影响[J].兵器材料科学与工程,2015,38(2):65-67.

2郑彬.铜模铸造钒基贮氢合金的电化学性能研究[J].热加工工艺,2015,44(1):66-68. 被引量:1

3罗永春,史亮,康龙,阎汝煦,孔令斌.La_(0.75)Mg_(0.25)Ni_(3.5-x)M_x(M=Si,Zn;x=0~0.5)储氢合金的相结构与电化学性能[J].兰州理工大学学报,2008,34(6):9-14. 被引量:2

4董小平,刘生龙,杨丽颖,王翠表,陈家熠,张羊换.熔体快淬对A_2B_7型La_(0.8)Mg_(0.2)Ni_(3.5)Co_(0.2)合金结构及电化学性能的影响[J].材料热处理学报,2014,35(4):1-6. 被引量:2

5李宝仁.热轧SiMnCr双相钢循环软化:硬化的微观过程[J].辽宁冶金,1997(6):49-50.

6唐仁衡,周顺,肖方明,王英,孙泰.热处理温度对La_(0.8)Ce_(0.2)(NiCoMnAl)_5储氢合金结构与性能的影响[J].材料导报,2014,28(14):114-116. 被引量:3

7李蒙,朱磊,尉海军,简旭宇.La-Mg-Ni系A_5B_(19)相储氢合金热处理工艺研究[J].稀有金属,2012,36(2):236-241. 被引量:7

8董小平,杨立清,杨丽颖,朱凯宁,王涛,王翠表.La-Mg-Ni-Co-Al-Ti合金电极的失效研究[J].材料热处理学报,2012,33(8):17-22.

9唐辉,张乐福,孙华.表面喷丸对800合金点蚀性能影响[J].腐蚀与防护,2012,33(10):853-855. 被引量:5

10董小平,杨丽颖,林玉芳,张羊换,王新林.制备工艺对La_(0.80)Mg_(0.20)Ni_(3.75)合金电极性能的影响[J].稀有金属与硬质合金,2010,38(1):11-15. 被引量:2

Basic Information:

DOI:

Chinese Library Classification Number:TG146.45[金属学及工艺—金属材料]

Citation Information:

La0.75Mg0.25Ni3.47Co0.2Al0.03 alloy was prepared by intermediate-frequency induction vacuum melting. The reasons for the efficacy loss of the alloy electrode were investigated by electrochemical and gaseous cycle experiments,SEM and XPS. The results show that capacity attenuation in both discharge and hydrogen absorption cycles takes place in rapid and slow stages. With cycling number increasing,the corrosive oxide on the surface of alloy particle increases during electrochemical cycling, and the contact resistance and charge transfer resistance first decrease and then increase. During gaseous hydrogen absorption and desorp- tion cycling,the crack of the alloy particle increases and the split extent enlarges. The main reason of the alloy electrode capacity decay is the oxidation and corrosion of La and Mg. Alloy particle pulverization ac- celerates the corrosion of La and Mg, and further deteriorates the cycling performance of the alloy electrode.

quote

GB/T 7714-2015 [1] DONG Xiao-ping, GENG Xiao-guang, YANG Li-ying, et al. Study on the Efficacy Loss of the La0.75Mg0.25Ni3.47Co0.2Al0.03 Hydrogen Storage Alloy Electrode[J]. Rare Metals and Cemented Carbides, 2011(3): 25-30.
MLA [1] DONG Xiao-ping, et al., "Study on the Efficacy Loss of the La0.75Mg0.25Ni3.47Co0.2Al0.03 Hydrogen Storage Alloy Electrode." Rare Metals and Cemented Carbides, no. 3, 2011, pp. 25-30.
APA [1] DONG Xiao-ping, GENG Xiao-guang, YANG Li-ying, SHI Xian, LU Xi-chao, & ZHONG Yang. (2011). Study on the Efficacy Loss of the La0.75Mg0.25Ni3.47Co0.2Al0.03 Hydrogen Storage Alloy Electrode. Rare Metals and Cemented Carbides(3), 25-30.
IEEE [1] DONG Xiao-ping, GENG Xiao-guang, YANG Li-ying, SHI Xian, LU Xi-chao, and ZHONG Yang, "Study on the Efficacy Loss of the La0.75Mg0.25Ni3.47Co0.2Al0.03 Hydrogen Storage Alloy Electrode," Rare Metals and Cemented Carbides, no. 3, pp. 25-30, 2011. keywords: {La0.75Mg0.25Ni3.47Co0.2Al0.03;hydrogen storage alloy;electrochemical cycle gaseous hydrogen ab- sorption and desorption cycle;oxidation corrosion;pulverization}