Preparation of Large-size Submicro-grained Cemented Carbide Anvils by Hot Isostatic Pressing AITranslate
Abstract AITranslate
YG10 X submicro-grained cemented carbide anvils with large-scale size above ?160 mm were prepared by compacting,dewaxing,vacuum sintering and hot isostatic pressing(HIP) treatment,using ultrafine-grained WC-Co spray-dried mixed powders as starting materials.The effects of the matched process of vacuum sintering with HIP treatment and different dewaxing atmosphere on properties and microstructure of the anvils were investigated.The ?188 mm anvil prepared by 200~300 ℃×40 h slow hydrogen continuous dewaxing and matched sintering process supplemented by 1 380 ℃ hot isostatic pressing has uniform microstructure,fine grains and stable performance,its transverse fracture strength of each part is higher than 4 100 MPa,and average service life is longer than 9 000~11 500 times.
KeyWords AITranslate
1邓瑞湘,汤波,肖俊玲,胡国程.影响硬质合金顶锤使用寿命的因素分析[J].湖南冶金,1995,23(4):15-18. 被引量：1
2李园园,徐银超,林江华,左锐,于涛,温光华,陈响明.EBSD在超细硬质合金WC晶粒尺寸统计中的应用[J].粉末冶金材料科学与工程,2015,20(2):162-167. 被引量：6
3贾攀,刘乾坤,何文江,戚燕杰,周亮良.合成金刚石用硬质合金顶锤的冷却方式对顶锤使用寿命及合成质量的影响[J].金刚石与磨料磨具工程,2015,35(4):56-59. 被引量：2
4袁明健,顾金宝.氢气脱蜡工艺与原料WC碳量的选择[J].硬质合金,2010,27(5):293-297. 被引量：2
5彭文.硬质合金六面顶大顶锤的质量控制[J].硬质合金,2000,17(4):225-230. 被引量：8
6王松顺.提高硬质合金顶锤使用寿命的途径及方法[J].超硬材料工程,2007,19(3):28-31. 被引量：4
7高新亮.亚微米硬质合金顶锤的研制[J].超硬材料工程,2010,22(1):13-17. 被引量：4
8韩奇钢,贾晓鹏,马红安,李瑞,张聪,李战厂,田宇.基于三维有限元法模拟分析六面顶顶锤的热应力[J].物理学报,2009(7):4812-4816. 被引量：3
9彭文,邓涛.硬质合金先进技术在大规格顶锤制造中的应用[J].超硬材料工程,2013,25(1):25-29. 被引量：5
1罗来马,汤俊宇,吴玉程.WC-Co硬质合金的成型工艺研究进展[J].机械工程学报,2023,59(8):60-73.
1刘文彬,裴新军,陈飞雄,熊宁,王铁军.φ175特大顶锤解剖分析及试样热等静压工艺研究[J].硬质合金,2019,36(5):374-380.
2唐启佳,李重典,李锐.添加锰对WC-8Co硬质合金组织和性能的影响[J].中国钨业,2019,34(6):30-35. 被引量：1
3范昆.硬质合金压力烧结炉H_2脱蜡停电自动充气保护装置设计[J].机械工程师,2018(3):61-62.
4王琦(编译).由气体雾化和热等静压制成的超级奧氏体不镑钢粉末冶金材料的性能[J].不锈,2020,0(1):48-50.
5屈鹏,宋嘉明,瞿宗宏,赖运金,梁书锦.脱气温度对Inconel718粉末热等静压制件性能的影响[J].中国新技术新产品,2019,0(23):61-63. 被引量：1
6刘乾坤,赵鹏,吴定雨,昝亚男,武周军,王卫康.基于主应力法对六面顶压机密封边受力的分析[J].超硬材料工程,2019,31(6):16-18. 被引量：3
7吴晓锋,赵晓明,赵伟,谢国印.热等静压冷速对SLM成形K536合金力学性能的影响[J].铸造技术,2020,41(2):115-120. 被引量：1
8杨建东.石墨烯增韧结构陶瓷材料研究进展[J].化学与粘合,2020,42(3):220-224. 被引量：1
9路坊海,郑凯,苏向东,陈肖虎,黄芳,王芝成,谷小菲,鄢青松.赤泥-废旧阴极高温协同处理资源化利用[J].轻金属,2020(3):9-12. 被引量：1
10刘强,刘阳,韦家蓓,谢腾飞,李江.Yb∶CaF2透明陶瓷的制备与性能研究[J].人工晶体学报,2020,49(5):799-803. 被引量：1
Basic Information:
DOI：
Chinese Library Classification Number:TG135.5[一般工业技术—材料科学与工程]
Citation Information:
YG10 X submicro-grained cemented carbide anvils with large-scale size above ?160 mm were prepared by compacting,dewaxing,vacuum sintering and hot isostatic pressing(HIP) treatment,using ultrafine-grained WC-Co spray-dried mixed powders as starting materials.The effects of the matched process of vacuum sintering with HIP treatment and different dewaxing atmosphere on properties and microstructure of the anvils were investigated.The ?188 mm anvil prepared by 200~300 ℃×40 h slow hydrogen continuous dewaxing and matched sintering process supplemented by 1 380 ℃ hot isostatic pressing has uniform microstructure,fine grains and stable performance,its transverse fracture strength of each part is higher than 4 100 MPa,and average service life is longer than 9 000~11 500 times.
quote
| GB/T 7714-2015 | [1] LIU Wen-bin, CHEN Fei-xiong, PEI Xin-jun, et al. Preparation of Large-size Submicro-grained Cemented Carbide Anvils by Hot Isostatic Pressing[J]. Rare Metals and Cemented Carbides, 2020(2): 82-89. |
| MLA | [1] LIU Wen-bin, et al., "Preparation of Large-size Submicro-grained Cemented Carbide Anvils by Hot Isostatic Pressing." Rare Metals and Cemented Carbides, no. 2, 2020, pp. 82-89. |
| APA | [1] LIU Wen-bin, CHEN Fei-xiong, PEI Xin-jun, XIONG Ning, & WANG Tie-jun. (2020). Preparation of Large-size Submicro-grained Cemented Carbide Anvils by Hot Isostatic Pressing. Rare Metals and Cemented Carbides(2), 82-89. |
| IEEE | [1] LIU Wen-bin, CHEN Fei-xiong, PEI Xin-jun, XIONG Ning, and WANG Tie-jun, "Preparation of Large-size Submicro-grained Cemented Carbide Anvils by Hot Isostatic Pressing," Rare Metals and Cemented Carbides, no. 2, pp. 82-89, 2020. keywords: {cemented carbide;large-size anvil;hot isostatic pressing;hydrogen dewaxing;vacuum sintering;microstructure;mechanical property} |