Research on a New Mixture Process of Tungsten Powder with Carbon AITranslate
Abstract AITranslate
Tungsten powder was mixing with carbon by double cone mixer and vertical high speed mixer, the effects of parameters of the new carbon addition process by double cone mixing and stirring mixing on the quality of W+C mixture were studied,and the uniformity of carbon distribution in W+C mixture was analyzed by range analysis.The results show that the uniformity of carbon distribution of W+C mixture produced by double cone mixing and stirring mixing process is better than that of traditional ball milling mixing process.The W+C mixture with good carbon uniformity can be produced under the conditions of 12 r/min operating velocity,50% filling rate,5hmixing time,alternating operation from positive to negative direction,and 4min stir mixing time.
KeyWords AITranslate
1田建华.粗颗粒钨粉配碳新工艺的研究[J].硬质合金,2006,23(2):79-83. 被引量：4
2陈文革.粉末混合质量的评定及影响因素[J].电工合金,1998(1):28-30. 被引量：7
1张华民,蒋福海.添加微量液体石蜡对超粗钨粉配炭及碳化效果的影响[J].稀有金属与硬质合金,2021,49(4):76-80.
1杨哲,汪磊.铸钢用水基消失模铸造涂料研究[J].铸造,2018,67(12):1076-1079. 被引量：4
2蓝敏俐.金刚石绳锯冷压齿生产工艺过程研究[J].智库时代,2018(51):135-137. 被引量：1
3张青.制造业企业存货管理研究——以浙江泰仑绝缘子有限公司为例[J].时代经贸,2019,17(3):56-57. 被引量：2
4孙世杰.美国金属粉末工业联合会与美国粉末冶金学会评选出2018年获奖论文[J].粉末冶金工业,2018,28(6):33-33.
5赖可溱,贺紫萍,布依婷,罗萌,唐湘云,苏招红,蒋红梅.基于黑米的荧光碳量子点的合成及性能表征[J].广州化工,2019,47(2):42-44.
6王军,赵琛,董彦,赵闯,朱磊.结构参数对Urea-SCR系统性能的影响研究[J].汽车工程,2019,41(1):29-35. 被引量：6
7黄泽宇,黄耀松,陈靖,郑丽丽.入口条件对D4合成石英玻璃的影响[J].燃烧科学与技术,2018,24(6):477-486. 被引量：3
8王金平,夏继红,汪颖俊,窦传彬,周之悦,叶继兵,刘瀚.山丘区中小河流滩地时空演化与扰动因子分析[J].中国农村水利水电,2018(12):66-69. 被引量：2
9邹庆华.金融机构债券交易行为特征分析——以湖南省为例[J].金融经济,2019(2):117-118. 被引量：2
10孙培永,李梦晨,周玉鹏,张胜红,姚志龙.脂肪酸甲酯加氢脱氧和加氢脱氮制备生物烷烃[J].精细化工,2018,35(12):2052-2057. 被引量：1
Basic Information:
DOI：
Chinese Library Classification Number:TG146.411[金属学及工艺—金属材料]
Citation Information:
Tungsten powder was mixing with carbon by double cone mixer and vertical high speed mixer, the effects of parameters of the new carbon addition process by double cone mixing and stirring mixing on the quality of W+C mixture were studied,and the uniformity of carbon distribution in W+C mixture was analyzed by range analysis.The results show that the uniformity of carbon distribution of W+C mixture produced by double cone mixing and stirring mixing process is better than that of traditional ball milling mixing process.The W+C mixture with good carbon uniformity can be produced under the conditions of 12 r/min operating velocity,50% filling rate,5hmixing time,alternating operation from positive to negative direction,and 4min stir mixing time.
quote
| GB/T 7714-2015 | [1] XIE Yong-cai, YU Bi-he. Research on a New Mixture Process of Tungsten Powder with Carbon[J]. Rare Metals and Cemented Carbides, 2018(6): 93-96. |
| MLA | [1] XIE Yong-cai, and YU Bi-he. "Research on a New Mixture Process of Tungsten Powder with Carbon." Rare Metals and Cemented Carbides, no. 6, 2018, pp. 93-96. |
| APA | [1] XIE Yong-cai, & YU Bi-he. (2018). Research on a New Mixture Process of Tungsten Powder with Carbon. Rare Metals and Cemented Carbides(6), 93-96. |
| IEEE | [1] XIE Yong-cai and YU Bi-he, "Research on a New Mixture Process of Tungsten Powder with Carbon," Rare Metals and Cemented Carbides, no. 6, pp. 93-96, 2018. keywords: {double cone mixing;stirring mixing;carbon addition;tungsten powder;carbon;the uniformity of carbon distribution} |