Layered MgxV2O5·nH2O as Cathode Material for High-Performance Aqueous Zinc Ion Batteries AITranslate

Fangwang Ming; Hanfeng Liang; Yongjiu Lei; Sharath Kandambeth; Mohamed Eddaoudi; Husam N. Alshareef;
King Abdullah University of Science and Technology (KAUST); King Abdullah University of Science and Technology (KAUST); King Abdullah University of Science and Technology (KAUST); King Abdullah University of Science and Technology (KAUST); King Abdullah University of Science and Technology (KAUST); King Abdullah University of Science and Technology (KAUST)
AITranslate
Publisher: ACS
Share Citation Information Add to Favorites

    Scan to share on WeChat or Moments

Use WeChat scan.
Share with WeChat friends or Moments

Abstract AITranslate

The performance of chemically intercalated V2O5 was found to strongly depend on the interlayer spacing, which is related to the radius of hydrated metal ion, which can be readily tuned by using different intercalated metals. We report a layered Mg2+-intercalated V2O5 as the cathode material for aqueous ZIBs. The large radius of hydrated Mg2+ (∼4.3 Å, compared with 3.8 Å of commonly used Li+) results in an interlayer spacing as large as 13.4 Å (against 11.07 Å for Li+-intercalated V2O5), which allows efficient Zn2+ (de)insertion. As a result, the obtained porous Mg0.34V2O5·0.84H2O cathodes work in a wide potential window of 0.1 to 1.8 V versus Zn2+/Zn, and can deliver high capacities of 353 and 264 mA h g–1 at current densities of 100 and 1000 mA g–1, respectively, along with long-term durability. Furthermore, the reversible Zn2+ (de)intercalation reaction mechanism is confirmed by multiple characterizations methods.

KeyWords AITranslate

No data

Basic Information:

DOI：https://doi.org/10.1021/acsenergylett.8b01423

Chinese Library Classification Number:

Citation Information:

The performance of chemically intercalated V2O5 was found to strongly depend on the interlayer spacing, which is related to the radius of hydrated metal ion, which can be readily tuned by using different intercalated metals. We report a layered Mg2+-intercalated V2O5 as the cathode material for aqueous ZIBs. The large radius of hydrated Mg2+ (∼4.3 Å, compared with 3.8 Å of commonly used Li+) results in an interlayer spacing as large as 13.4 Å (against 11.07 Å for Li+-intercalated V2O5), which allows efficient Zn2+ (de)insertion. As a result, the obtained porous Mg0.34V2O5·0.84H2O cathodes work in a wide potential window of 0.1 to 1.8 V versus Zn2+/Zn, and can deliver high capacities of 353 and 264 mA h g–1 at current densities of 100 and 1000 mA g–1, respectively, along with long-term durability. Furthermore, the reversible Zn2+ (de)intercalation reaction mechanism is confirmed by multiple characterizations methods.

quote

GB/T 7714-2015 [1] Fangwang Ming, Hanfeng Liang, Yongjiu Lei, et al. ACS Energy Letters, 2018(3). DOI:10.1021/acsenergylett.8b01423.
MLA [1] Fangwang Ming, et al., ACS Energy Letters, no. 3, 2018, https://doi.org/10.1021/acsenergylett.8b01423.
APA [1] Fangwang Ming, Hanfeng Liang, Yongjiu Lei, Sharath Kandambeth, Mohamed Eddaoudi, & Husam N. Alshareef. (2018). ACS Energy Letters(3). https://doi.org/10.1021/acsenergylett.8b01423
IEEE [1] Fangwang Ming, Hanfeng Liang, Yongjiu Lei, Sharath Kandambeth, Mohamed Eddaoudi, and Husam N. Alshareef, ACS Energy Letters, no. 3, 2018, doi: 10.1021/acsenergylett.8b01423.