Effects of the Hydrophobic Block Length Ratio of Poly(vinylbenzyl N-methylpiperidinium carbonate)-b-polyethylene-b-poly(vinylbenzyl N-methylpiperidinium carbonate) Block Copolymers for Anion Exchange Membrane Electrolysis AITranslate

Basic Information:

DOI：https://doi.org/10.1021/acsapm.3c00414

Chinese Library Classification Number:

Citation Information:

Electrolysis of water to produce hydrogen from renewable electricity is an extremely attractive strategy to reduce energy dependence on fossil fuels. Development of membrane and ionomer materials that maintain high performance with long lifetimes is needed. We developed and investigated the performance and durability of a series of polyethylene-based ABA triblock copolymer anion exchange ionomer and membrane (AEI, AEM) materials for anion exchange membrane water electrolysis. Poly(vinylbenzyl N-methylpiperidinium carbonate)-b-polyethylene-b-poly(vinylbenzyl N-methylpiperidinium carbonate) was synthesized with different hydrophobic/hydrophilic block ratios (1.02:1, 2.58:1, and 4.46:1) resulting in a range of ion exchange capacities (1.1–1.8 meq g–1) and water swelling (23–154%) characteristics. All AEMs showed full anionic dissociation, as evidenced by linear Arrhenius correlations, and excellent carbonate conductivity of 8–94 mS cm–1 at 50 °C. Hydrophilic phase separation may offer superior chemical durability by only wetting the ion-conducting region of the polymer and avoiding attack at the nonwetted backbone. We evaluated the performance and durability of these AEMs as a function of hydrophobic polyethylene (PE) content. The AEM containing the least amount of PE displayed the highest performance of 1 A cm–2 at 2.3 V but degraded at 40 mV h–1 before catastrophically failing after <3 h at 0.5 A cm–2. With greater PE-containing AEMs, the degradation rate was reduced by 3 orders of magnitude with only a 0.2 V increase in voltage. Constant current electrolysis for 50 h resulted in a voltage change of 0.3 mV h–1 in a single-cell water electrolyzer and 1 M potassium carbonate. In a 600 h test, the voltage change in the final 200 h was impressively low for an experimental film, 58 μV h–1. Postmortem analysis indicated that the membrane did not thin and that water becomes more tightly hydrogen-bound in the polymer after electrolysis.